This study presents the removal of phosphate from aqueous solution using a new silver nanoparticles-loaded tea activated carbon (AgNPs-TAC) material. In order to reduce costs, the tea activated carbon was produced from tea residue. Batch adsorption experiments were conducted to evaluate the effects of impregnation ratio of AgNPs and TAC, pH solution, contact time, initial phosphate concentration and dose of AgNPs-AC on removing phosphate from aqueous solution. Results show that the best conditions for phosphate adsorption occurred at the impregnation ratio AgNPs/TAC of 3% w/w, pH 3, and contact time lasting 150 min. The maximum adsorption capacity of phosphate on AgNPs-TAC determined by the Langmuir model was 13.62 mg/g at an initial phosphate concentration of 30 mg/L. The adsorption isotherm of phosphate on AgNPs-TAC fits well with both the Langmuir and Sips models. The adsorption kinetics data were also described well by the pseudo-first-order and pseudo-second-order models with high correlation coefficients of 0.978 and 0.966, respectively. The adsorption process was controlled by chemisorption through complexes and ligand exchange mechanisms. This study suggests that AgNPs-TAC is a promising, low cost adsorbent for phosphate removal from aqueous solution.

This study investigated the phenomenon and mechanism of adsorption of methylene green 5 (MG5) on three pristine biosorbents: golden shower pod (GS), coconut shell (CC), and orange peel (OP). The results showed that the biosorbents possessed low specific surface areas, but abundant functional groups. Adsorption was strongly affected by the solution’s pH and ionic strength. As revealed in the kinetic study, equilibrium was rapidly established, requiring low activation energies; a removal rate of 30%–87% was achieved within 1 min. The maximum Langmuir adsorption capacities at 30°C exhibited the following order: GS (106 mg/g) > OP (92 mg/g) > CC (59 mg/g). Thermodynamic experiments suggested that the adsorption occurred spontaneously (−ΔG°) and exothermically (−ΔH°). The primary adsorption mechanisms involved electrostatic attraction, hydrogen bonding formations, and n-π interaction. Thermogravimetric analysis (TGA) revealed that three biopolymer components (i.e., hemicellulose, cellulose, and lignin) played controlling roles in the adsorption process. Thus, these three agricultural residues can be considered potential low-cost adsorbents for efficient dye adsorption applications.