Pd/Al₂O₃ catalyst of the “crust” type with Pd loading of 0.03 wt.% was prepared by the deposition of 2 nm Pd particles on the outer surface of the alumina support using laser electrodispersion (LED). This technique differs from a standard laser ablation into a liquid in that the formation of monodisperse nanoparticles occurs in the laser torch plasma in a vacuum. As is found, the LED-prepared catalyst surpasses Pd-containing three-way catalysts, obtained by conventional chemical synthesis, in activity and stability in CO oxidation under prompt thermal aging conditions. Thus, the LED-prepared Pd/Al₂O₃ catalyst showed the best thermal stability up to 1000 °C. The present research is focused on the study of the high-temperature evolution of the Pd/Al₂O₃ catalyst in two reaction mixtures by a set of physicochemical methods (transmission electron microscopy, X-ray photoelectron spectroscopy, and diffuse reflectance UV-vis spectroscopy). In order to follow the dispersion of the Pd nanoparticles during the thermal aging procedure, the testing reaction of ethane hydrogenolysis was also applied. The possible reasons for the high stability of LED-prepared catalysts are suggested.

New Pt-Co catalysts of hydrogen purification from CO impurities for fuel cells were fabricated via the deposition of monodispersed 1.7 nm Pt nanoparticles using laser electrodispersion on Co-modified ZSM-5 prepared by the Co(CH₃COO)₂ impregnation. The structure of prepared Pt-Co zeolites was studied by low-temperature N₂ sorption, TEM, EDX, and XPS methods. The comparative analysis of samples with different Pt (0.01–0.05 wt.%) and Co (2.5–4.5 wt.%) contents on zeolites with the ratio of Si/Al = 15, 28, and 40 was performed in the CO-PROX reaction in H₂-rich mixture (1%CO + 1%O₂ + 49%H₂ + 49%He). The synergistic catalytic action of Pt and Co on zeolite surface makes it possible to completely remove CO from a mixture with hydrogen in a wide temperature range from 50 to 150 °C; the high efficiency of designed composites with low Pt loading is maintained for a long time. The enhancement of PROX performance originates from the formation of new active sites for the CO oxidation at the Pt-Co interfaces within zeolite channels and at the surface. In terms of their activity, stability, and selectivity, such composites are significantly superior to known supported Pt-Co catalysts.

Electrochemical experiments with a rotating disk electrode are used to measure specific catalytic activity of Pt/C structures in the oxygen reduction reaction at the density of Pt nanoparticles on the glassy carbon support surface below one monolayer. The specific activity maximum is found at the coverage of about 0.4 monolayer. An explanation of the observed dependence is suggested that is based on consideration of the relationship between the surface density and charge state of the system of metallic catalyst particles. A numeric model is developed that describes charge transfer in the catalyst structure due to the difference in the work functions between the metal nanoparticles and support with account for the discrete nature of the nanoparticle charging and their mutual polarization. Calculations show that the carbon support coverage by Pt particles of about 0.4 monolayer corresponds to the largest amount of charged particles with the maximum energy of electrons, which provides the maximum catalyst activity and explains the dependence observed in the experiment.

Zeolites and metal-doped zeolites are now widely considered as low-temperature hydrocarbon traps to be a part of emission control systems in automobiles. However, due to the high temperature of exhaust gases, the thermal stability of such sorbent materials is of great concern. To avoid the thermal instability problem, in the present work, laser electrodispersion was used to deposit Pd particles on the surface of ZSM-5 zeolite grains (SiO₂/Al₂O₃ = 55 and SiO₂/Al₂O₃ = 30) to obtain Pd/ZSM-5 materials with a Pd loading as low as 0.03 wt.%. The thermal stability was evaluated in a prompt thermal aging regime involving thermal treatment at temperatures up to 1000 °C in a real reaction mixture (CO, hydrocarbons, NO, an excess of O₂, and balance N₂) and a model mixture of the same composition with the exception of hydrocarbons. Low-temperature nitrogen adsorption and X-ray diffraction analysis were used to examine the stability of the zeolite framework. Special attention was paid to the state of Pd after thermal aging at varied temperatures. By means of transmission electron microscopy, X-ray photoelectron spectroscopy, and diffuse reflectance UV–Vis spectroscopy, it was shown that palladium, having been initially located on the surface of zeolite, undergoes oxidation and migrates into the zeolite’s channels. This enhances the trapping of hydrocarbons and their subsequent oxidation at lower temperatures.

Experimental results on the laser ablation of the highly oriented pyrolytic graphite by using light pulses of an Nd:YAG laser (pulse width 25 ns, pulse energy 220 mJ) are presented. Analysis of the...

The paper shows the possibility of describing the charge-discharge characteristics of supercapacitors with porous carbon electrodes using a simple equivalent circuit with constant capacitances and resistances. Using numerical simulation, it is shown that there is a relationship between the parameters of the equivalent circuit and the pore structure of the electrode material. The simulation results also indicate the inhomogeneous nature of the charging of various groups of pores of the electrode material in the structure of the supercapacitor.