In recent days the rising concern over environmental pollution with excessive use of synthetic materials has led to various eco-friendly innovations. Due to the organic nature, abundance and higher strength, natural fibers are gaining a lot of interest among researchers and are also extensively used by various industries to produce ecological products. Natural fibers are widely used in the composite industry as an alternative to synthetic fibers for numerous applications and new sources of fiber are continuously being explored. In this study, a fiber extracted from the Furcraea foetida (FF) plant is characterized for its feasibility as a reinforcement to fabricate polymer composite. The results show that the fiber has a density of 0.903 ± 0.07 g/cm³, tensile strength (σ_t) of 170.47 ± 24.71 MPa and the fiber is thermally stable up to 250 °C. The chemical functional groups and elements present in the FF fiber are evaluated by conducting Fourier transform infrared spectroscopy (FT-IR) and energy dispersive spectroscopy (EDS). The addition of FF fibers in epoxy reduced the density (13.44%) and hardness (10.9%) of the FF/Epoxy (FF/E) composite. However, the void content (V_c < 8%) and water absorption (WA: < 6%) rate increased in the composite. The FF/E composite with 30% volume of FF fibers showed maximum σ_t (32.14 ± 5.54 MPa) and flexural strength (σ_f: 80.23 ± 11.3 MPa).

In the last few decades, natural composite materials have been considered one of the highly sustainable ecological alternatives for reducing the consumption of synthetic materials. Today, research on natural fiber composites is the main thrust for their use in various industrial applications. Further, continuous research works are being carried out to utilize natural composites as an alternative to synthetic materials. However, the inhomogeneity of composites, delamination, fiber pullout, higher surface roughness (SR) and dimensional inaccuracy under traditional machining have led the attention towards non-traditional machining, such as abrasive water jet machining, to achieve high-quality components. Hence, in this study, an experimental analysis based on the design of experiments is conducted on the machinability of a hybrid rice straw/Furcraea foetida composite under abrasive water jet machining (AWJM). Further, the concentration of the rice straw and the AWJ process parameters are varied, and their effects on the quality of machining is evaluated. The experimental trials are designed based on the Taguchi L₂₇ orthogonal array, followed by an analysis of variance (ANOVA). From extensive experimentations, the concentration of rice straw is observed to be the most contributing (93.5%) factor to the SR. The traverse speed (TS) shows the highest percentage contributions of 93.13%, 55.50 and 55.70% to the material removal rate (MRR) and the top (T_KW) and bottom kerf widths (B_KW), respectively. However, the interaction between the fiber concentration and traverse speed gives the maximum contribution (35.04%) to the kerf taper (K_T). A second-order response surface model is generated to study the effects of the process parameters on the SR, MRR, T_KW, B_KW and K_T in any experimental domain. Finally, the microstructural characteristics of the machined surfaces, such as micro-cracks, debonding, and fiber pullout, are discussed.

Managing rice crop stubble is one of the major challenges witnessed in the agricultural sector. This work attempts to investigate the physical, mechanical, and liquid absorption properties of rice straw (RS)-reinforced polymer composite for assessing its suitability to use as an ayurvedic treatment table. This material is expected to be an alternative for wooden-based ayurvedic treatment tables. The results showed that the addition of rice straw particles (RS_p) up to 60% volume in epoxy reduced the density of the composite material by 46.20% and the hardness by 15.69%. The maximum tensile and flexural strength of the RS_p composite was 17.53 MPa and 43.23 MPa, respectively. The scanning electron microscopy (SEM) analysis showed deposits of silica in the form of phytoliths in various size and shapes on the outer surface of RS. The study also revealed that the water absorption rate (WA) was less than 7.8% for the test samples with 45% volume of RS_p. Interestingly the test samples showed greater resistance to the absorption of Kottakal Dhanvantaram Thailam (<2%). In addition, the developed samples showed resistance towards bacterial and fungal growth under the exposure of treatment oils and water.