Adding short steel fibers into slag-based geopolymer mortar and concrete is an effective method to enhance their mechanical properties. The fracture properties of steel fiber-reinforced slag-based geopolymer concrete/mortar (SGC/SGM) and unreinforced control samples were compared through three-point bending (TPB) tests. The influences of steel fiber volume contents (1.0%, 1.5% and 2.0%) on the fracture properties of SGC and SGM were studied. Load-midspan deflection (P-δ) curves and load-crack mouth opening displacement (P-CMOD) curves of the tested beams were recorded. The compressive and splitting tensile strengths were also tested. The fracture energy, flexural strength parameters, and fracture toughness of steel fiber-reinforced SGC and SGM were calculated and analyzed. The softening curves of steel fiber-reinforced SGC and SGM were determined using inverse analysis. The experimental results show that the splitting tensile strength, fracture energy, and fracture toughness are significantly enhanced with fiber incorporation. A strong correlation between the equivalent and residual flexural strengths is also observed. In addition, the trilinear strain-softening curves obtained by inverse analysis predict well of the load-displacement curves recorded from TPB tests.

Fiber-reinforced polymer (FRP) confining jackets offer an attractive solution for the seismic retrofit of RC columns. For the accurate prediction of strength and ductility of FRP-confined RC columns, it is necessary to understand interactions between the FRP jacket and the RC column at all deformation levels under seismic loading. In particular, when the transverse steel reinforcement consists of widely spaced steel stirrups or spirals, the longitudinal steel reinforcing bars (rebars) are likely to develop buckling deformations despite the lateral support provided by the FRP-confined concrete. This paper presents a theoretical study into the buckling behavior of longitudinal steel rebars embedded in FRP-confined concrete subjected to monotonic axial compression. In the theoretical model, a beam-on-elastic foundation idealization is used, where the steel rebars are laterally supported by elastic springs representing the FRP-confined cover concrete. To evaluate the stiffness of the elastic springs, a curved beam model is proposed. Predictions from the theoretical model are compared with test results, demonstrating the reliability of the theoretical model. A parametric study is then presented to examine the influence of three key factors (i.e., spring stiffness, yield strength of steel, and slenderness ratio of rebar) on the overall compressive stress–strain response of laterally supported steel rebars. Finally, an empirical compressive stress–strain model considering the effect of buckling deformation is proposed for steel rebars embedded in FRP-confined concrete subjected to monotonic axial compression and validated through comparisons with the test results.

This paper presents finite element (FE) modeling of the debonding behavior of fiber reinforced polymer (FRP)-to-concrete interfaces subject to mixed-mode loading, which is realized through a peeling test of FRP composites externally bonded onto a concrete substrate. A cohesive zone model (CZM) is implemented into the FE model to represent the behavior of the FRP-to-concrete interface. Two element schemes (orthotropic plane stress element and beam element) were employed to simulate the behavior of FRP composite plate in the peeling test. The orthotropic plane stress element scheme, bearing a clear physical background and with an easy definition of the material property parameters following the composite mechanics, is found to be superior to the beam element scheme, and thus is utilized to conduct parametric studies. The influences of the peeling angle, the interfacial parameters (i.e., the configuration of the cohesive zone models, the interfacial damage initiation law (DIL), the interfacial damage evolution law (DEL), the coupling of mode-I and mode-II components), on the mixed-mode failure of the FRP-concrete-interface are carefully investigated. The results showed that the mode I component plays a critical role in the debonding failure of FRP-to-concrete interfaces even when the peeling angle is very small. The failure of FRP-to-concrete interface transits promptly from a mode II-dominated one to a mode I-dominated one when the peeling angle increases to a relatively small value (e.g., 4 degree) and subsequently the peeling force (i.e., the debonding strength of FRP) decreases dramatically. Such mixity of the mode I and mode II components should be appropriately considered for refining the analysis of FRP-strengthened RC beams and the FRP debonding strength design, for which a pure mode II interfacial failure was usually assumed.

Polyethylene terephthalate (PET) fiber has attracted significant attention for reinforced concrete (RC) structure rehabilitation due to its large rupture strain (LRS; more than 7%) characteristic and recyclability from waste plastic bottles. This study presents a dynamic tensile test of PET fiber bundles performed using a drop-weight impact system. Results showed that the tensile strength and the elastic modulus of the PET fiber bundles increased, whereas the failure strain and the toughness decreased with the increasing strain rate from 1/600 to 160 s⁻¹. In addition, the performance of concrete confined with the PET fiber-reinforced polymer (FRP) under impact loading was investigated based on a 75 mm-diameter split Hopkinson pressure bar (SHPB) device and a drop-weight apparatus. For the SHPB test, owing to the large rupture strain property of PET FRP, the PET FRP-confined concrete exhibited significantly better performance under impact loading compared to its counterpart confined with carbon FRPs (CFRPs). During the drop-weight test, the confinement of the PET FRP composites to the concrete columns as external jackets not only improved the peak impact force, but also prolonged the impact process.

This paper aimed to determine the softening laws and fracture toughness of slag-based geopolymer (SG) concrete and mortar (SGC and SGM) as compared to those of Portland cement (PC) concrete and mortar (PCC and PCM). Using three-point bending (TPB) tests, the load vs. mid-span displacement, crack mouth opening displacement, and crack tip opening displacement curves (P-d, P-CMOD, and P-CTOD curves) were all recorded. Bilinear softening laws of the PC and SG series were determined by inverse analysis. Furthermore, the cohesive toughness was predicted using an analytical fracture model. The cohesive toughness obtained by experimental study was consistent with that predicted by analytical method, proving the correctness of the tension softening law obtained from inverse analysis. In addition, both initial and unstable fracture toughness values of SG mortar were lower than those of PC mortar given the same compressive strength. Moreover, the initial fracture toughness of SG concrete was generally lower than that of PC concrete, whereas the unstable fracture toughness exhibited an opposite trend.