MXene has drawn widespread attention as a potential material for electrode use in capacitive deionization (CDI). However, the applications of MXene are limited by its property of low electrical capacity. Herein, a MnO₂/MXene composite was firstly evaluated in a capacitive deionization system, in which the MnO₂ acts as intercalation-type pseudocapacitive electrodes to enhance the electrical capacity, and MXene provides an electron conduction highway network that improves the charge transfer of the MnO₂. The result showed that the low-crystallinity MnO₂ with irregular particles was well-distributed on the surface of the MXene. The desalination capacity of 30.5 mg·g⁻¹ is achieved at a voltage window of 1.2 V, which was higher than that of the reported pure MXene and MnO₂. The electrical double-layer (EDL) capacitive and the diffusion-controlled processes are the main charge storage mechanisms, and the EDL contribution provides 50.3% to the total capacitance. This result suggests a promising direction for further applying a MnO₂/MXene composite in CDI.

The safe disposal of hazardous waste from zinc hydrometallurgy, such as jarosite residue, is crucial for the sustainable development of the industry. The chemical, structural and morphological properties of jarosite residue from zinc smelting were studied by a combination of various characterizations, and environmental stability was evaluated using the toxicity characteristic leaching procedure (TCLP), Chinese standard leaching tests (CSLT) and long-term leaching experiments (LTLE). Phase composition analysis revealed that zinc ferrite and sodium jarosite were the main phases present in the jarosite residue. TCLP and CSLT analyses indicated that the Zn and Pb contents exceeded their respective toxicity identification standards by more than 30 times and 8 times, respectively, exceeding the threshold values of the standard. The LTLE results demonstrated that Pb concentrations continued to exceed the standard limits, even after long contact times. This study has paramount significance in the prediction of jarosite residue stability and the evaluation of its potential for secondary environmental pollution.