In order to explore the effect of printing parameter configurations on the forming performance of Digital Light Processing (DLP) 3D printed samples, printing experiments were carried out on the enhanced adhesion and efficient demolding of DLP 3D printing devices. The molding accuracy and mechanical properties of the printed samples with different thickness configurations were tested. The test results show that when the layer thickness increases from 0.02 mm to 0.22 mm, the dimensional accuracy in the X and Y directions increases first and then decreases, while the dimensional accuracy in the Z direction decreases, and the dimensional accuracy is the highest when the layer thickness is 0.1 mm. The mechanical properties of the samples decline with an increasing layer thickness of the samples. The mechanical properties of the 0.08 mm layer thickness are the best, and the tensile, bending, and impact properties are 22.86 Mpa, 48.4 Mpa, and 35.467 KJ/m², respectively. Under the condition of ensuring molding accuracy, the optimal layer thickness of the printing device is determined to be 0.1 mm. The analysis of the section morphology of samples with different thicknesses illustrates that the fracture of the sample is a river-like brittle fracture, and there are no defects such as pores in the section of samples.

A novel forming method of enhanced adhesion-efficient demolding integration is proposed to solve the problems of weak adhesion between the initial forming layer and the printing platform as well as the excessive stripping force at the bottom of the liquid tank when the printing platform rises. Therefore, a digital light processing (DLP) 3D printing forming device equipped with a porous replaceable printing platform and a swing mechanism for the liquid tank is manufactured and verified by experiments. The experimental results show that the porous printing platform can enhance the adhesion between the initial forming layer and the printing platform and improve the demolding efficiency of the forming device. In addition, the pull-out design of the printing platform plate reduces the maintenance cost of the forming device. Therefore, the device has a good application prospect.

Powder laying is a necessary procedure during powder bed additive manufacturing (PBAM), and the quality of powder bed has an important effect on the performance of products. Because the powder particle motion state during the powder laying process of biomass composites is difficult to observe, and the influence of the powder laying process parameters on the quality of the powder bed is still unclear, a simulation study of the biomass composite powder laying process during powder bed additive manufacturing was conducted using the discrete element method. A discrete element model of walnut shell/Co-PES composite powder was established using the multi-sphere unit method, and the powder-spreading process was numerically simulated using two different powder spreading methods (rollers/scrapers). The results showed that the quality of powder bed formed by roller laying was better than that formed by scrapers with the same powder laying speed and powder laying thickness. For both of the two different spreading methods, the uniformity and density of the powder bed decreased as spreading speed increased, although the spreading speed had a more important influence on scraper spreading compared to roller spreading. As powder laying thickness increased, the powder bed formed by the two different powder laying methods became more uniform and denser. When the powder laying thickness was less than 110μm, the particles were easily blocked at the powder laying gap and are pushed out of the forming platform, forming many voids, and decreasing the powder bed’s quality. When the powder thickness was greater than 140 μm, the uniformity and density of the powder bed increased gradually, the number of voids decreased, and the quality of the powder bed improved.

High-quality wood products and valuable wood crafts receive everyone’s favor with the rapid development of the economy. In order to improve the cutting surface quality of wood forming parts, the cutting experiment of renewable Fraxinus mandshurica was conducted by waterjet-assisted CO2 laser (WACL) technology. A quadratic mathematical model for describing the relationship between surface roughness changes and cutting parameters was established. The effects of cutting speed, flow pressure and laser power on the kerf surface roughness of Fraxinus mandshurica when cutting transversally were discussed by response surface method. The experimental results showed that kerf surface roughness decreased under a lower laser power, higher cutting speed and higher flow pressure. When the cutting speed was 30 mm/s, flow pressure was 1.58 MPa and laser power was 45 W, the actual surface roughness of the optimized Fraxinus mandshurica was 2.41 μm, and it was in accord with the theoretically predicted surface roughness value of 2.54 μm, so the model fitted the actual situation well. Through the analysis of 3D profile morphology and micromorphology, it was concluded that the optimized kerf surface of Fraxinus mandshurica was smoother, the cell wall was not destroyed and the tracheid was clear. It provides the theoretical basis for wood micromachining.