Ground tire rubber (GTR) is a product obtained by grinding worn tire treads before retreading them or via the cryogenic or ambient temperature milling of end-of-life tires (ELTs). The aim of this study is to evaluate if calcium carbonate can be substituted by GTR and, if so, to what extent. Different types of ground tire rubber are incorporated in an EPDM (ethylene–propylene–diene–rubber) model compound as partial or complete substitutes of calcium carbonate. The raw compounds and the vulcanizates are characterized to identify the limits. In general, it is apparent that increasing amounts of GTR and larger particles degrade the mechanical properties. The GTR also influences the vulcanization kinetics by reducing the scorch time up to 50% and vulcanization time up to nearly 80%. This is significant for production processes. The compounds with one-third substitution with the smaller-particle-size GTR show mostly similar or even better properties than the reference.

SCIEPublish is an international open-access journal publishing service provider run by SCIE Publishing Limited, dedicated to supporting and inspiring scientists or institutions/societies who aspire to publish high-quality journals.

Ni–Ti alloys are used as functional materials in numerous sectors such as aerospace, automotive engineering, medical technology, and consumer goods. Their properties in terms of shape memory effect and superelasticity offer a great potential for innovative smart products. However, forming and machining of these alloys into concrete products is challenging. Assembling plain structures by laser welding to complex product shapes offers an economical alternative in many cases, but can be associated with negative effects, such as reduction of strength, development of brittle intermetallic compounds, alteration of transformation temperatures, and modification of shape memory effects and superelastic behavior. Against this background, investigations on laser welding of Ni55/Ti45 foil with a thickness of 125 µm by a fiber laser were conducted. Supported by methods of design of experiments, optimal parameters were determined with respect to laser power, welding speed, focus position, and beam oscillation, and the welding results were analyzed concerning the microstructure and mechanical characteristics of the welded joints. The effect of laser beam oscillation was investigated for the first time for the welding of this alloy. Due to the very low thickness, the preparation of the foils for the microstructure characterization is quite demanding. Best results were obtained by ion milling. Fracture surfaces and the influence of the welding were also investigated.

SCIEPublish is an international open-access journal publishing service provider run by SCIE Publishing Limited, dedicated to supporting and inspiring scientists or institutions/societies who aspire to publish high-quality journals.

Pyrolysis is becoming increasingly important in the context of recycling and the volume of end‐of‐life tires worldwide. Sustainable carbon black (sCB), which is produced from pyrolysis oil instead of crude oil, and recovered carbon black (rCB), which is the remaining solid from pyrolysis, are promising secondary raw materials for rubber compounds as a substitute for industrial carbon black produced from fossil resources. This study investigates the possibility of substituting carbon black N550 partially or fully in an EPDM (Ethylene Propylene Diene Monomer) sealing compound. rCB contains impurities that affect the properties of the compound. Aging at higher temperatures, in the presence of oxygen is studied. The properties of the compounds are evaluated after heat treatment in air at different temperatures for up to 6 weeks. The results show that sCB is very close to N550 as a raw material and in terms of its in‐rubber properties. Due to the impurities, rCB alters the cross‐linking density and structure of the polymer‐sulfur network (shift to polysulfidic structure). Lower reinforcement is also observed, which is related to weaker polymer‐filler (decrease of I_3/1 for sCB by 3% and rCB by 43% related to vCB) and filler‐filler interactions. Aging effects are also more pronounced in the compounds containing rCB.

Three-dimensional printing is ideally suited to produce unique and complex shapes. In this study, the material properties of polysiloxanes, commonly named silicones, produced additively by two different methods, namely, multi-jet fusion (MJF) and material extrusion (ME) with liquid printing heads, are investigated. The chemical composition was compared via Fourier-transform infrared spectroscopy, evolved gas analysis mass spectrometry, pyrolysis gas chromatography coupled to mass spectrometry, and thermogravimetry (TGA). Density and low-temperature flexibility, mechanical properties and crosslink distance via freezing point depression were measured before and after post-treatment at elevated temperatures. The results show significant differences in the chemical composition, material properties, as well as surface quality of the tested products produced by the two manufacturing routes. Chemical analysis indicates that the investigated MJF materials contain acrylate moieties, possibly isobornyl acrylate linking branches. The hardness of the MJF samples is associated with crosslinking density. In the ashes after TGA, traces of phosphorus were found, which could originate from initiators or catalysts of the curing process. The ME materials contain fillers, most probably silica, that differ in their amount. It is possible that silica also plays a role in the processing to stabilize the extrusion strand. For the harder material, a higher crosslink density was found, which was supported also by the other tested properties. The MJF samples have smooth surfaces, while the ME samples show grooved surface structures typical for the material extrusion process. Post-treatment did not improve the material properties. In the MJF samples, significant color changes were observed.