Increasing environmental pollution in urban areas has been endangering the survival of carbonate stones in monuments and statuary for many decades. Numerous conservation treatments have been applied for the protection and consolidation of these works of art. Most of them, however, either release dangerous gases during curing or show very little efficacy. Bacterially induced carbonate mineralization has been proposed as a novel and environmentally friendly strategy for the conservation of deteriorated ornamental stone. However, the method appeared to display insufficient consolidation and plugging of pores. Here we report thatMyxococcus xanthus-induced calcium carbonate precipitation efficiently protects and consolidates porous ornamental limestone. The newly formed carbonate cements calcite grains by depositing on the walls of the pores without plugging them. Sonication tests demonstrate that these new carbonate crystals are strongly attached to the substratum, mostly due to epitaxial growth on preexisting calcite grains. The new crystals are more stress resistant than the calcite grains of the original stone because they are organic-inorganic composites. Variations in the phosphate concentrations of the culture medium lead to changes in local pH and bacterial productivity. These affect the structure of the new cement and the type of precipitated CaCO₃polymorph (vaterite or calcite). The manipulation of culture medium composition creates new ways of controlling bacterial biomineralization that in the future could be applied to the conservation of ornamental stone.

Field emission scanning electron microscopy (FESEM), two-dimensional X-ray diffraction (2D-XRD), and transmission electron microscopy coupled with selected area electron diffraction (TEM-SAED) analyses of the reactant/product textural relationship show that the thermal decomposition of Iceland spar single crystals according to the reaction CaCO_3(s) → CaO_(s) + CO_2(g) is pseudomorphic and topotactic. This reaction begins with the formation of a mesoporous structure made up of up to four sets of oriented rod-shaped CaO nanocrystals on each rhombohedral cleavage face of the calcite pseudomorph. The four sets formed on (101̅4)_calcite display the following topotactic relationships: (1) (12̅10)_calcite//(110)_CaO; (2) (1̅104)_calcite^⊥ (110)_CaO; (3) (1̅018)_calcite//(110)_CaO; and (4) (01̅14)_calcite^⊥(110)_CaO; with [841]_calcite//[11̅0]_CaO in all four cases. At this stage, the reaction mechanism is independent of PCO₂ (i.e., air or high vacuum). Strain accumulation leads to the collapse of the mesoporous structure, resulting in the oriented aggregation of metastable CaO nanocrystals (~5 nm in thickness) that form crystal bundles up to ~1 μm in cross-section. Finally, sintering progresses up to the maximum T reached (1150 °C). Oriented aggregation and sintering (plus associated shrinking) reduce surface area and porosity (from 79.2 to 0.6 m²/g and from 53 to 47%, respectively) by loss of mesopores and growth of micrometer-sized pores. An isoconversional kinetic analysis of non-isothermal thermogravimetric data of the decomposition of calcite in air yields an overall effective activation energy E_α = 176 ± 9 kJ/mol (for α > 0.2), a value which approaches the equilibrium enthalpy for calcite thermal decomposition (177.8 kJ/mol). The overall good kinetic fit with the F₁ model (chemical reaction, first order) is in agreement with a homogeneous transformation. These analytical and kinetic results enable us to propose a novel model for the thermal decomposition of calcite that explains how decarbonation occurs at the atomic scale via a topotactic mechanism, which is independent of the experimental conditions. This new mechanistic model may help reinterpret previous results on the calcite/CaO transformation, having important geological and technological implications.