Elementary processes of electro mass transfer in the nanocomposite polymer electrolyte system by pulse field gradient, spin echo NMR spectroscopy and the high-resolution NMR method together with electrochemical impedance spectroscopy are examined. The new nanocomposite polymer gel electrolytes consisted of polyethylene glycol diacrylate (PEGDA), salt LiBF₄ and 1—ethyl—3—methylimidazolium tetrafluoroborate (EMIBF₄) and SiO₂ nanoparticles. Kinetics of the PEGDA matrix formation was studied by isothermal calorimetry. The flexible polymer–ionic liquid films were studied by IRFT spectroscopy, differential scanning calorimetry and temperature gravimetric analysis. The total conductivity in these systems was about 10⁻⁴ S cm⁻¹ (−40 °C), 10⁻³ S cm⁻¹ (25 °C) and 10⁻² S cm⁻¹ (100 °C). The method of quantum-chemical modeling of the interaction of SiO₂ nanoparticles with ions showed the advantage of the mixed adsorption process, in which a negatively charged surface layer is formed from Li⁺ BF₄^— ions on silicon dioxide particles and then from ions of the ionic liquid EMI⁺ BF₄⁻. These electrolytes are promising for use both in lithium power sources and in supercapacitors. The paper shows preliminary tests of a lithium cell with an organic electrode based on a pentaazapentacene derivative for 110 charge–discharge cycles.

The article considers the effect of the solvate environment of the lithium cation in various aprotic solvents.The redox reactions of electrodes made from a polymeric condensation product of triquinoyl with 1,2,4,5-tetraaminobenzene are studied. A 1 M LiPF₆ solution was used as an electrolyte, in either ethylene carbonate/dimethyl carbonate (EC/DMC) or tetraglyme. Based on the electrochemical studies and quantum chemical modeling, it was shown that the desolvation of lithium cations in the tetraglyme-based electrolyte makes it possible to obtain a capacity close to the theoretical one (up to 546 mAh g⁻¹) and only 125 mAh g⁻¹ for the EC/DMC electrolyte. This decrease is due to the fact that the lithium cation adds to the functional groups of the organic material with two dimethyl carbonate molecules, as well as the PF₆⁻ anion.