This article presents the effect of the addition of condensed tannins, used as a reticulation agent, on the polymerization of furfuryl alcohol during wood furfurylation, as well as the effect of these condensed tannins on the thermal stability of modified wood. Three kinds of dicarboxylic acids (adipic acid, succinic acid, and tartaric acid), as well as glyoxal, used as model of a wood reticulation agent, were used to catalyze the polymerization of furfuryl alcohol or tannin-furfuryl alcohol solutions. Impregnation of furfuryl alcohol or tannin-furfuryl alcohol solution into the wood, followed by curing at 103 °C for a specific duration, was performed for the wood modification. The thermal stability of the obtained tannin-furfuryl alcohol polymers and their corresponding modified woods was investigated. The leaching resistance and dimensional stability of the modified woods were also evaluated. Results indicated that the partial substitution of furfuryl alcohol by the tannins improved the polymerization reactivity in conditions where furfuryl alcohol alone did not lead to the formation of a solid polymeric material. The thermal stability and leaching resistance of the furfurylated wood in the presence of tannins were improved. Dimensional stability was also improved for furfurylated samples, but the effect of tannin addition was not so obvious, depending on the acidic catalyst used.

This paper presents mechanical properties and biological durability properties against soft-rot (soil bed test) and subterranean termites (grave-yard test) of the wood modified with a vinylic derivative of glycerol or polyglycerol and maleic anhydride at different curing conditions. Wood modification was performed through impregnation of European beech (Fagus sylvatica) with an aqueous solution of polyglycerol maleate, glycerol maleate, or maleic anhydride at 10 or 20% w/w concentration, followed with curing under oven heating (OHT) in an open system (120°C, 150°C, or 220°C) or under heat pressurised steam (HPS) at 150°C in a closed system. Results revealed that almost all modified wood presented higher modulus of elasticity (MOE) values than untreated wood, however, modulus of rupture (MOR) and work to maximum load in bending (WMLB) decreased considerably. Biological durability in the soil bed test against soft-rot indicated that almost all modified wood was specified as “durable” to “very durable”. However, among the treatments, the wood modified with polyglycerol maleate/glycerol maleate/maleic anhydride at 20% under OHT 150°C or the wood modified at lower additive concentration (10%) under OHT 220°C presented excellent durability against subterranean termites within a period of 328 days in the field.

Short rotation teak (SRT) has a diameter of around 30 cm at the age of 15 years; however, the wood still has low quality, especially in dimensional stability and biological durability. The objective of this study was to improve dimensional stability and biological durability of SRT through modification treatment using non-biocide chemicals, citric acid (CA) and benzophenone tetracarboxylic acid (BPTCA). SRT sapwood was impregnated by 20% and 40% of CA or BPTCA followed by heating in the oven at 150 °C for 2 h. Dimensional stability, strength, surface characteristics and durability against termite attacks of the modified woods were evaluated. Results show that dimensional stability as anti-swelling efficiency (ASE) increased by an average of 46% (CA) and 50% (BPTCA) after treatments. Durability against termites showed that the modified woods were categorized to be class 1 (very durable). Fourier Transform Infrared (FTIR) and X-ray Diffraction observations indicated a possible chemical reaction between the wood components with CA and BPTCA. The water-based acrylic and oil-based alkyd contact angle values of the modified woods were lower than 90°, indicating their high wetting ability against the varnish liquids. The treatment can be applied to improve the quality of SRT for high-quality wood product utilization.

This study aimed to enhance tropical fast-growing tree species’ resistance to subterranean termite (Coptotermes curvignathus) attacks through the manufacturing of polystyrene glued-laminated timber (glulam). Three young tropical wood species, namely manii (Maesopsis eminii), mangium (Acacia mangium), and rubber-wood (Hevea brasiliensis), were cut into laminae. After drying, the laminae were impregnated with styrene monomer, then polymerized using potassium peroxydisulfate as a catalyst and heat. The polystyrene-impregnated laminae were constructed using isocyanate glue and a cold press for three-layered glulam. Untreated or control glulam and solid wood specimens were also prepared. The specimens of each wood species and wood products (solid wood, control glulam, and polystyrene glulam) were exposed to the termite in a laboratory test according to Indonesian standards. The results showed that mangium wood had better resistance to the termite attack than manii and rubber-wood, with both of those woods performing the same. Among the wood products, the glulams were equal and had higher resistance to the termite attack than solid wood. To enhance the termite resistance of polystyrene glulam, we suggest that the polymer loading of polystyrene on each lamina should be increased. In our evaluation of the products’ order of priority, polystyrene glulam emerged as performing best towards subterranean termites attack.