This work presents research on thin magnetron-sputtered platinum (Pt) films deposited over commercial gas diffusion electrodes and applied to convert and pressurize hydrogen in an electrochemical hydrogen pump. The electrodes were integrated into a membrane electrode assembly with a proton conductive membrane. Their electrocatalytic efficiency toward hydrogen oxidation and hydrogen evolution reactions was studied in a self-made laboratory test cell by means of steady-state polarization curves and cell voltage measurements (U/j and U/p_diff characteristics). The achieved current density at a cell voltage of 0.5 V, the atmospheric pressure of the input hydrogen, and a temperature of 60 °C was more than 1.3 A cm⁻². The registered increase in the cell voltage with the increasing pressure was only 0.05 mV bar⁻¹. Comparative data with commercial E-TEK electrodes reveal the superior catalyst performance and essential cost reduction of the electrochemical hydrogen conversion on the sputtered Pt films.

In this research, a thin layer of multi-metallic non-precious catalyst is prepared by electroplating from an electrolyte bath containing Ni, Co, and Fe sulfates over pressed commercial nickel foam electrode. The composition of the deposited catalytic film and its morphology are characterized by scanning electron microscopy (SEM) with energy dispersion X-ray (EDX) techniques. The efficiency of the prepared binder-free electrodes for electrochemical water splitting is investigated in a self-designed short water electrolysis stack with zero-gap configuration of the integrated single cells and hybrid electrical connections. The separator used is a commercial Zirfon Perl 500 membrane, doped with 25% KOH. The performance of the catalyst, the single cells, and the developed electrolyzer stack are examined by steady state polarization curves and stationery galvanostatic stability tests in the temperature range 20 °C to 80 °C. The NiFeCoP multi-metallic alloy demonstrates superior catalytic efficiency compared to the pure nickel foam electrodes and reliable stability with time. The single cells in the stack show identical performance and the cumulative stack parameters strictly follow the theoretical considerations. The applied hybrid electrical connections enable scaling of both the stack voltage and the passing current, which in turn ensures flexibility with regard to the input power and the hydrogen production capacity.

Solid-state supercapacitors with gel electrolytes have emerged as a promising field for various energy storage applications, including electronic devices, electric vehicles, and mobile phones. In this study, nanocomposite gel membranes were fabricated using the solution casting method with perfluorosulfonic acid (PFSA) ionomer dispersion, both with and without the incorporation of 10 wt.% montmorillonite (MMT). MMT, a natural clay known for its high surface area and layered structure, is expected to enhance the properties of supercapacitor systems. Manganese oxide, selected for its pseudocapacitive behavior in a neutral electrolyte, was synthesized via direct co-precipitation. The materials underwent structural and morphological characterization. For electrochemical evaluation, a two-electrode Swagelok cell was employed, featuring a carbon xerogel negative electrode, a manganese dioxide positive electrode, and a PFSA polymer membrane serving as both the electrolyte and separator. The membrane was immersed in a 1 M Na₂SO₄ solution before testing. A comprehensive electrochemical analysis of the hybrid cells was conducted and compared with a symmetric carbon/carbon supercapacitor. Cyclic voltammetric curves were recorded, and galvanostatic charge–discharge tests were conducted at various temperatures (20, 40, 60 °C). The hybrid cell with the PFSA/MMT 10 wt.% exhibited the highest specific capacitance and maintained its hybrid profile after prolonged cycling at elevated temperatures, highlighting the potential of the newly developed membrane.

This study explores the synthesis and characterization of platinum (Pt), nickel (Ni), and cobalt (Co)-based electrocatalysts using the sol–gel method. The focus is on the effect of different support materials on the catalytic performance in alkaline media. The sol–gel technique enables the production of highly uniform electrocatalysts, supported on carbon-based substrates, metal oxides, and conductive polymers. Various characterization techniques, including X-ray diffraction (XRD) and scanning electron microscopy (SEM), were used to analyze the structure of the synthesized materials, while their electrochemical properties, which are relevant to their application in unitized regenerative fuel cells (URFCs), were investigated using cyclic voltammetry (CV) and linear sweep voltammetry (LSV). This hydrogen energy-converting device integrates water electrolyzers and fuel cells into a single system, reducing weight, volume, and cost. However, their performance is constrained by the electrocatalyst’s oxygen bifunctional activity. To improve URFC efficiency, an ideal electrocatalyst should exhibit high oxygen evolution (OER) and oxygen reduction (ORR) activity with a low bifunctionality index (BI). The present study evaluated the prepared electrocatalysts in an alkaline medium, finding that Pt25-Co75/XC72R and Pt75-Co25/N82 demonstrated promising bifunctional activity. The results suggest that these electrocatalysts are well-suited for both electrolysis and fuel cell operation in anion exchange membrane-unitized regenerative fuel cells (AEM-URFCs), contributing to improved round-trip efficiency.

The work presents novel composite catalytic materials—Ni and Co deposited on Magneli phase titania—and describes their complex characterization and integration into membrane electrode assemblies to produce hydrogen by electrochemical water splitting in cells with anion exchange membranes (AEMEC). Chemical composition, surface structure, and morphology were characterized by XRD and SEM analysis. The activity in the evolution of the partial electrode reactions of hydrogen (HER) and oxygen (OER) was assessed in an aqueous alkaline electrolyte (25 wt.% KOH) using linear sweep voltammetry. The interactive role of the support was investigated and discussed. Among the tested samples, the sample with 30 wt.% Co (Co30/MPT) demonstrated superior performance in the OER. The reaction started at 1.65 V, and at 1.8 V, the current density reached 75 mA cm⁻². The HER is most efficient on the sample containing 40 wt.% Ni (Ni40/MPT), where the current density reaches 95 mA at a potential of −0.5 V. The change in catalytic efficiency compared to that of the unsupported Ni and Co is due to synergism resulting from electronic interactions between the transition metal having a hyper-d-electron character and hypo-d-electron support. The pre-selected catalysts were integrated in membrane electrode assembly (MEA) using commercial and laboratory-prepared anion-conductive membranes and tested in a custom-made AEMEC. The performance was compared to that of MEA with a commercial carbon-supported Pt catalyst. It was found that the MEA with newly prepared catalysts demonstrated better performance in long-term operation (50 mA cm⁻² at 1.8 V in a 60 h durability test), which, combined with the higher cost efficiency, gave credence to considering this combination of materials as promising for AEMEC applications.

In this study, mono- and bimetallic platinum (Pt), palladium (Pd) and Pt-Pd nanoparticles were synthesized using the wet sol–gel method, employing a carbon-based XC72R as catalytic carrier. The overall metal content was set at 40 wt.% at varying Pt:Pd ratios. Characterization of the morphology and surface structure was conducted through scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), Brunauer–Emmett–Teller (BET) and X-ray diffraction (XRD) analyses. The electrochemical performance and catalytic activity against the hydrogen evolution reaction (HER) were assessed in a three-electrode cell for screening purposes, as well as in a prototype cell of an electrochemical hydrogen pump/compressor (EHP/C) where the catalysts served as cathodes, while the anode was Pt/XC72 40% wt. with 0.38 mg_Pt·cm⁻² within a membrane electrode assembly (MEA) with a 180 µm thick Nafion 117 proton-conductive membrane. The results obtained indicated superior catalytic activity of the bimetallic catalysts in comparison to the pure metal samples. Further electrochemical tests in an EHP/C cell at varying differential pressures in the range of 0–3 bar revealed stable behavior and high current density, reaching approximately 0.7 A cm⁻² at 60 °C. The accelerated durability tests performed demonstrated excellent stability of the synthesized composite catalysts. These findings underscore the potential of Pt-Pd nanoparticles as efficient catalysts with sustainable performance for electrochemical hydrogen pumping/compressing applications.