A novel route for the valorization of waste into valuable products was developed. Surgical masks commonly used for COVID 19 protection by stopping aerosol and droplets have been widely used, and their disposal is critical and often not properly pursued. This work intended to transform surgical masks into platinum group metal‐free electrocatalysts for oxygen reduction reaction (ORR) and hydrogen evolution reaction (HER) as well as into crude oil. Surgical masks were subjected to controlled‐temperature and ‐atmosphere pyrolysis, and the produced char was then converted into electrocatalysts by functionalizing it with metal phthalocyanine of interest. The electrocatalytic performance characterization towards ORR and HER was carried out highlighting promising activity. At different temperatures, condensable oil fractions were acquired and thoroughly analyzed. Transformation of waste surgical masks into electrocatalysts and crude oil can open new routes for the conversion of waste into valuable products within the core of the circular economy.

Making a consistency with the objectives of circular economy, herein, waste pistachios shells were utilized for the development of hydrogen evolution reaction (HER) and oxygen reduction reaction (ORR) electrocatalysts which are the key bottleneck in the technological evolution of electrolyzers and fuel cells, respectively. As an alternative to scarce and expensive platinum-group-metal (PGM) electrocatalysts, metal nitrogen carbons (MNCs) are emerging as a promising candidate for both aforementioned electrocatalysis where iron and nickel are the metal of choice for ORR and HER, respectively. Therefore, FeNCs and NiNCs were fabricated utilizing inedible pistachio shells as a low-cost biosource of carbon. The steps involved in the fabrication of electrocatalyst were correlated with electrochemical performance in alkaline media. Encouraging onset potential of ~ 0.88 V vs RHE with a possibility of a 2 + 2 reaction pathway was observed in pyrolyzed and ball-milled FeNC. However, HF etching for template removal slightly affected the kinetics and eventually resulted in a relatively higher yield of peroxide. In parallel, the pyrolyzed NiNC demonstrated a lower HER overpotential of ~ 0.4 V vs RHE at − 10 mA cm⁻². Nevertheless, acid washing adversely affected the HER performance and consequently, very high overpotential was witnessed.

Following the core theme of a circular economy, a novel strategy to upcycle cigarette butt waste into platinum group metal (PGM)-free metal nitrogen carbon (M-N-C) electrocatalysts for oxygen reduction reaction (ORR) is presented. The experimental route was composed of (i) the transformation of the powdered cigarette butts into carbonaceous char via pyrolysis at 450 °C, 600 °C, 750 °C and 900 °C, (ii) the porosity activation with KOH and (iii) the functionalization of the activated chars with iron (II) phthalocyanine (FePc). The electrochemical outcomes obtained by the rotating disk electrode (RRDE) technique revealed that the sample pyrolyzed at 450 °C (i.e., cig_450) outperformed the other counterparts with its highest onset (E_on) and half-wave potentials (E_1/2) and demonstrated nearly tetra-electronic ORR in acidic, neutral and alkaline electrolytes, all resulting from the optimal surface chemistry and textural properties.