Atmospheric-pressure plasma (APP) has advantages for enhancing the adhesion of polymers and has to provide uniform, efficient treatment, which also limits the recovery effect of treated surfaces. This study investigates the effects of APP treatment on polymers that have no oxygen bonded in their structure and varying crystallinity, aiming to assess the maximum level of modification and the post-treatment stability of non-polar polymers based on their initial structure parameters, including the crystalline–amorphous structure. An APP reactor simulating continuous processing operating in air is employed, and the polymers are analyzed using contact angle measurement, XPS, AFM, and XRD. APP treatment significantly enhances the hydrophilic character of the polymers, with semicrystalline polymers exhibiting adhesion work values of approximately 105 mJ/m² and 110 mJ/m² for 0.5 s and 1.0 s exposure, respectively, while amorphous polymers reach approximately 128 mJ/m². The maximum average oxygen uptake is around 30%. Short treatment times induce the roughening of the semicrystalline polymer surfaces, while the amorphous polymer surfaces become smoother. The polymers exhibit a limit to their modification level, with 0.5 s exposure being optimal for significant surface property changes. The treated surfaces remain remarkably stable, with the contact angle only reverting by a few degrees toward that of the untreated state.

This study’s aim is a comparison of the plasma-induced effects on polymers exposed in helium and argon gaseous environments in a pulsed dielectric barrier discharge at atmospheric pressure. Cellulose-based and synthetic polymers are tested with regard to a range of parameters, such as wettability, adhesion, surface energy and polarity, the oxygen amount in their structure, and surface morphology. The surface properties are analyzed by contact angle measurements, X-ray photoelectron spectroscopy, and scanning electron microscopy images. The results point to the efficient and remarkably stable modifications of the plasma-exposed surfaces, such as their enhanced adhesion, surface energy, and oxygen incorporation. Additionally, plasma provides significant oxygen uptake in cellulose-based materials that bear already prior to treatment a high amount of oxygen in their structure. The comparison between the properties of the non-permeable, homogeneous, smooth-surface synthetic polymer and those of the loosely packed, porous, heterogeneous cellulose-based polymers points to the different rates of plasma-induced modification, whereby a progressive alteration of cellulosic surface properties over much larger ranges of exposure durations is noted. Present experimental conditions ensure mild treatments on such sensitive material, such as paper, and this is without alterations of the surface morphology and the physical degradation of the material over a large range of treatment duration.