Rare earth elements and transition elements are widely used in aluminum alloys, magnesium alloys and copper alloys due to their unique microalloying effects. With regard to in-depth research on the grain refinement characteristics of rare earth elements and transition elements, the combination of grain refinement and microalloying in the master alloys has a great impact on the theories and technical research of refinement, and the broadening of the application field of master alloys. This paper first summarizes the grain refinement mechanisms and analyzes the effects of rare earth elements and transition elements on the grain refinement of aluminum and aluminum alloys, and summarizes the elements suitable for the preparation of Al-M master alloys and their refinement mechanism.

A novel Al-Mg-Si aluminum alloy with the addition of the micro-alloying element Er and Zr that was promptly quenched after extrusion has been studied. The solid solution and aging treatment of the novel alloy are studied by observing the microstructure, mechanical properties, and strengthening mechanism. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques are employed to examine the changes in the microstructure resulting from various solid solution treatments and aging treatments. The best strengthening effect can be achieved when the solubility of the MgSi phase and precipitate β″ (Mg₂Si phase) is at their maximum. The addition of Er and Zr elements promotes the precipitation of the β″ phase and makes the b″ phase more finely dispersed. The aging strengthening of alloys is a comprehensive effect of the dislocation cutting mechanism and bypass mechanism, the joint effect of diffusion strengthening of Al₃(Er,Zr) particles and the addition of Er and Zr elements promoting the precipitation strengthening of β″ phases. In this paper, by adding Er and Zr elements and exploring the optimal heat treatment system, the yield strength of the alloy reaches 437 MPa and the tensile strength reaches 453 MPa after solid solution treatment at 565 °C/30 min and aging at 175 °C/10 h.

The influence of grain size on the corrosion behavior of pure aluminum and the defect density and diffusion coefficient of surface passive films were investigated using electron backscatter diffraction (EBSD) and electrochemical testing techniques, based on the point defect model (PDM). Samples with three different grain sizes (23 ± 11, 134 ± 52, and 462 ± 203 μm) were obtained by annealing at different temperatures and times. The polarization curves and electrochemical impedance spectroscopy results for the pure aluminum in the 3.5% NaCl solution showed that with decreasing grain size, the corrosion current (i_corr) decreased monotonously, giving rise to a noble corrosion potential and a large polarization resistance. The Motte–Schottky results showed that the passive films that formed on pure aluminum with fine grains of 23 ± 11 μm had a low density (3.82 × 10²⁰ cm⁻³) of point defects, such as oxygen vacancies and/or metal interstitials, and a small diffusion coefficient (1.94 × 10⁻¹⁷ cm²/s). The influence of grain size on corrosion resistance was discussed. This work demonstrated that grain refinement could be an effective approach to achieving high corrosion resistance of passive metals.