In this paper, the SiC/SiC high-pressure turbine twin guide vanes were fabricated using the chemical vapor infiltration (CVI) method. Cyclic thermal shock tests at different target temperatures (i.e., 1400, 1450, and 1480 °C) in a gas environment were conducted to investigate the damage mechanisms and failure modes. During the thermal shock test, large spalling areas appeared on the leading edge and back region. After 400 thermal shock cycles, the spalling area of the coating at the basin and back region of the guide vane was more than 30%, and the whole guide vane turned gray, due to the formation of SiO₂. When the thermal shock temperature increased from 1400 to 1450 and 1480 °C, the spalling area of the basin and the back region of the guide vane did not increase significantly, but the delamination occurred at the tenon, upper surface of the guide vane near the trailing edge of the guide vane. Through the X-ray Computed Tomography (XCT) analysis for the guide vanes before and after thermal shock, there was no obvious damage inside of guide vanes. The oxidation of SiC coating and the formation of SiO₂ protects the internal fibers from oxidation and damage. Further investigation on the effect of thermal shock on the mechanical properties of SiC/SiC composites should be conducted in the future.

We have experimentally demonstrated an optical fiber Mach-Zehnder interferometer (MZI) structure formed by a few-mode photonic crystal fiber (PCF) for curvature measurement and inscribed a fiber Bragg grating (FBG) in the PCF for the purpose of simultaneously measuring temperature. The structure consists of a PCF sandwiched between two multi-mode fibers (MMFs). Bending experimental results show that the proposed sensor has a sensitivity of −1.03 nm/m⁻¹ at a curvature range from 10 m⁻¹ to 22.4 m⁻¹, and the curvature sensitivity of the embedded FBG was −0.003 nm/m⁻¹. Temperature response experimental results showed that the MZI’s wavelength, λ_a, has a sensitivity of 60.3 pm/°C, and the FBG’s Bragg wavelength, λ_b, has sensitivity of 9.2 pm/°C in the temperature range of 8 to 100 °C. As such, it can be used for simultaneous measurement of curvature and temperature over ranges of 10 m⁻¹ to 22.4 m⁻¹ and 8 °C to 100 °C, respectively. The results show that the embedded FBG can be a good indicator to compensate the varying ambient temperature during a curvature measurement.

In this paper, the 12k T-700^TM Multiaxial-Warp-Knitting–Needle (MWK–N) C/SiC composite and pin were designed and fabricated using the isothermal chemical vapor infiltration (ICVI) method. The composite’s microstructure and mechanical properties were examined by subjection to tensile and interlaminar shear tests. Three types of double-shear tests were conducted for C/SiC pins, including shear loading perpendicularly, along, and at 45° off-axial to the lamination. The fracture surface of the tensile and shear failure specimens was observed under scanning electronic microscope (SEM). The relationships between the composite’s microstructure, mechanical properties, and damage mechanisms were established. The composite’s average tensile strength was σ_uts = 68.3 MPa and the average interlaminar shear strength was τ_u = 38.7 MPa. For MWK–N–C/SiC pins, the double-shear strength was τ_u = 76.5 MPa, 99.7 MPa, and 79.6 MPa for test types I, II, and III, respectively. Compared with MWK–C/SiC pins, the double-shear strength of MWK–N–C/SiC pins all decreased, i.e., 26.7%, 50.8%, and 8% for test types I, II, and III, respectively. The MWK–N–C/SiC composite and pins possessed high interlaminar shear strength and double-shear strength, due to the needled fiber in the thickness direction, low porosity (10–15%), and high composite density (2.0 g/cm³).