Biomedical and Pharmacology Journal (BPJ) is an international, open access, peer reviewed, quarterly research journal.

Background. Implant insertion in regions with poor bone quantity, such as the posterior maxilla, is potentially associated with an increased rate of implant failure. Calcium sulfate can be used as the coating material for commercially pure titanium (CpTi) and as the bone graft material around implants when bound to eggshell powder to enhance the bone quality and quantity of bone defect regions. This study performed a torque removal test to evaluate the effectiveness of eggshell powder as a bone substitute for filling bone defects around CpTi-coated implants coated with nanocrystalline calcium sulfate. Materials and Methods. Eighty screw implant designs were used in the tibiae of 20 white New Zealand rabbits. A total of uncoated 20 screws constituted the control group, and the remaining 60 screws coated with nano calcium sulfate nanoparticles were used as the experimental groups as follows: 20 screws coated with nano calcium sulfate were used alone in the tibiae without gaps around them, 20 screws coated with nano calcium sulfate were used with the gaps made around them and filled with eggshell powder as the bone graft material, and 20 screws coated with nano calcium sulfate were used with the gaps made around them left unfilled. Results. After 2 to 6 weeks of healing, a significant improvement in bone regeneration and an increase in torque removal values were observed when the bone defect around the CpTi implant coated with nano calcium sulfate was filled with eggshell powder as the bone substitute. Conclusions. Nano calcium sulfate particles applied through the dip-coating method can successfully work as the coating material of CpTi implants. These particles work in synergy with eggshell powder to act as the bone graft around the implants.

Background: The best material for dental implants is polyetherketoneketone (PEKK). However, this substance is neither osteoinductive nor osteoconductive, preventing direct bone apposition. Modifying the PEKK with bioactive elements like strontium hydroxyapatite is one method to overcome this (Sr-HA). Due to the technique's capacity to provide better control over the coating's properties, RF magnetron sputtering has been found to be a particularly useful technique for deposition. Materials and methods : With specific sputtering conditions, the RF magnetron technique was employed to provide a homogeneous and thin coating on Polyetherketoneketone substrates.. the coatings were characterized by Contact angle, adhesion test, X-ray diffraction (XRD), atomic force microscope and Elemental Analysis with Energy Dispersive X-Ray (EDX) Results : indicated that strontium hydroxyapatite had successfully deposited onto the surface with significant improvement in the wettability value to provide a suitable environment for cell attachment, spreading, proliferation, and differentiation Conclusion: Coating PEKK with RF magnetron sputtering can provide homogeneous surfaces laying the groundwork for improving PEKK's potential bioactivity, such as surface wettability. Wetting qualities are critical in implantable materials and are used to predict future osseointegration success.

Biomedical and Pharmacology Journal (BPJ) is an international, open access, peer reviewed, quarterly research journal.

Background. Bone healing is a complex and dynamic process that represents a well-orchestrated series of biological events of cellular recruitment, proliferation, and differentiation. The use of medicinal plants in bone healing has attracted increasing interest because of their lower side effects. Punica granatum seed oil (PSO) contains high levels of phenolic compounds, promotes osteoblast function, and plays an important role in bone remodeling. A gelatin sponge (Spongostan) is a hemostatic agent that is extensively applied as scaffolds in engineering and as drug carriers in the medical field. This study aimed to evaluate the effectiveness of PSO for bone healing enhancement. Twenty adult male New Zealand rabbits, weighing an average of 1.52kg, were used in this study. Three intrabony holes were created in the tibiae of each animal, which were filled with a gelatin sponge (GS group) and combined gelatin sponge and PSO (GS/PSO group). Holes without material application were designated as the control group (C group). The animals were sacrificed at the healing duration (24 weeks) to prepare bone specimens for histological and histomorphometric analyses. Results. Histological findings indicated that the bone defects in the GS/PSO group showed more bone formation, mineralization, and maturation compared with the C and GS groups. Multiple group differences for bone cells showed a highly significant difference among all groups in the 2- and 4-week healing periods except for the C/GS and GS/GS/PSO groups at 4-weeks duration. Furthermore, highly significant results were obtained between both durations regarding the trabecular area, trabecular number, and bone marrow area. Conclusion. The study revealed that the combined application of GS and PSO was more effective in enhancing bone regeneration and accelerating bone healing compared with the other groups.