The need of light weight alloys for future transportation industry puts Sc and Ti under a sudden demand. While these metals can bring unique and desired properties to alloys, lack of reliable sources brought forth a supply problem which can be solved by valorization of the secondary resources. Bauxite residue (red mud), with considerable Ti and Sc content, is a promising resource for secure supply of these metals. Due to drawbacks of the direct leaching route from bauxite residue, such as silica gel formation and low selectivity towards these valuable metals, a novel leaching process based on oxidative leaching conditions, aiming more efficient and selective leaching but also considering environmental aspects via lower acid consumption, was investigated in this study. Combination of hydrogen peroxide (H₂O₂) and sulfuric acid (H₂SO₄) was utilized as the leaching solution, where various acid concentrations, solid-to-liquid ratios, leaching temperatures and times were examined in a comparative manner. Leaching with 2.5 M H₂O₂: 2.5 M H₂SO₄ mixture at 90 °C for 30 min was observed to be the best leaching conditions with suppressed silica gel formation and the highest reported leaching efficiency with high S/L ratio for Sc and Ti; 68% and 91%; respectively.

Due to its alkalinity, red mud produced by the Bayer process may affect both the environment and human health. For this reason, its further utilization instead of disposal is of great importance. Numerous methods have already been studied for hydrometallurgical treatment of red mud, especially for the recovery of various metallic components such as iron, aluminum, titanium or rare earth elements. This study focuses on the extraction of titanium from red mud and in particular the mineralogical changes, induced by leaching. Sulfuric acid, hydrochloric acid and their combination have been utilized as leaching agents with the same leaching parameters. It has been determined that sulfuric acid is the best candidate for the red mud treatment in terms of titanium leaching efficiency at the end of 2 h with a value of 67.3%. Moreover, samples from intermediate times of reaction revealed that leaching of Ti exhibit various reaction rates at different times of reaction depending on acid type. In order to explain differences, X-ray Diffraction (XRD), scanning electron microscope (SEM) and QEMSCAN techniques were utilized. Beside titanium oxide (TiO₂) with available free surface area, a certain amount of the TiO₂ was detected as entrapped in Fe dominating oxide. These associations between Ti and Fe phases were used to explain different leaching reaction rates and a reaction mechanism was proposed to open a process window.

Nanostructured zinc oxide (ZnO) particles were synthesized by the one step Ultrasonic Spray Pyrolysis (USP) process from nitrate salt solution (Zn(NO₃)₂·6H₂O). Various influential parameters, from Zn(NO₃)₂·6H₂O concentrations (0.01875–0.0375 M) in the initial solution, carrier gas (N₂) flow rates (0.5–0.75 L/min) to reaction temperature (400–800 °C), were tested to investigate their role on the final ZnO particles’ morphology. For this purpose, Scanning Electron Microscopy (SEM), High Resolution Transmission Electron Microscopy (HRTEM) and (Selected Area Electron Diffraction) SAED techniques were used to gain insight into how the ZnO morphology is dependent on the USP process. It was revealed that, by certain parameter selection, different ZnO morphology could be achieved, from spherical to sphere-like structures assembled by interwoven nanoplate and nanoplate ZnO particles. Further, a more detailed crystallographic investigation was performed by XRD and Williamson-Hall (W-H) analysis on the ZnO with unique and non-typical planar morphology that was not reported before by USP synthesis. Moreover, for the first time, a flexible USP formation model was proposed, ending up in various ZnO morphologies rather than only ideal spheres, which is highly promising to target a wide application area.

This article explains the mechanism of the metal/oxide core-shell Ag/TiO₂ and Au/TiO₂ nanoparticle formation via one-step ultrasonic spray pyrolysis (USP) by establishing a new model. The general knowledge on the standard “droplet-to-particle” (DTP) mechanism, nucleation, and growth processes of noble metals, as well as physical and chemical properties of core and shell materials and experimental knowledge, were utilized with the purpose of the construction of this new model. This hypothesis was assessed on silver (Ag)/titanium oxide (TiO₂) and gold (Au) TiO₂ binary complex nanoparticles’ experimental findings revealed by scanning electron microscopy (SEM), focused ion beam (FIB), high-resolution transmission electron microscopy (HRTEM), and simulation of crystal lattices. It was seen that two mechanisms run as proposed in the new model. However, there were some variations in size, morphology, and distribution of Ag and Au through the TiO₂ core particle and these variations could be explained by the inherent physical and chemical property differences of Ag and Au.