The loss of a permanent first molar in adolescent patient creates a need for early space maintenance and restoration of function. To ascertain function and esthetics, immediate treatments include interim restorative approaches. This paper describes a conservative, functional and cost-effective bridge as an interim restoration after the loss of permanent first molar in an early adolescent dentition.

Background and Objectives: Nickel–titanium (Niti) instruments have enhanced root canal cleaning in primary teeth, but file fractures are still common. Materials and Methods: This study evaluated the cyclic fatigue resistance of 120 Niti files from four different systems, A: Kedo SG (n = 30); B: Neoendo Pedoflex (n = 30); C: Pedoflex Waldent files (n = 30); and D: Vortex Blue files (n = 30). All the files had similar tip diameters (0.25 mm) and tapers (0.4%) and underwent heat treatment during manufacturing. Cyclic fatigue tests showed notable variations in cycles to fracture (NCF) across groups. All fracture surfaces of the files were assessed through scanning electron microscopy. Results: The mean values achieved in the experimental groups (A, B, C) were less than those in the control Group D (976.90 ± 1085.19). Files in Group A demonstrated the highest NCF (697.01 ± 420.09), while Pedoflex files in Group C showed the lowest values (203.88 ± 155.46). Statistical analysis using the Mann–Whitney test revealed significant differences between Group C and Groups A, B, and D and no differences among Groups A, B, and D. Conclusions: These findings suggest that Kedo SG and Neoendo Pedoflex files offer comparable cyclic fatigue resistance to Vortex Blue files. In contrast, Pedoflex Waldent files exhibit lower resistance to fracture.

Nickel-titanium (Niti) instruments have enhanced root canal cleaning in primary teeth, but file fractures are still common. This study evaluated the cyclic fatigue resistance of 120 Niti files from four different systems, A: Kedo SG (n=30); B: Neoendo Pedoflex (n=30); C: Pedoflex Waldent files (n=30) and D: Vortex Blue files (n=30). All the files had similar tip diameters (0.25 mm) and tapers (0.4%) and underwent heat treatment during manufacturing. Cyclic fatigue tests showed notable variations in cycles to fracture (NCF) across groups. All fracture surfaces of the files were assessed through scanning electron microscopy. The mean values achieved in the experimental groups (A, B, C) were less than those in the control group D (976.90 ± 1085.19). Files in Group A demonstrated the highest NCF (697.01 ± 420.09), while Pedoflex files in Group C showed the lowest values (203.88 ± 155.46). Statistical analysis using the Mann-Whitney test revealed significant differences between groups A, B, and D compared to Group C. Still, no differences among groups A, B, and D. These findings suggest that Kedo SG and Neoendo Pedoflex files offer comparable cyclic fatigue resistance to Vortex Blue files. In contrast, Pedoflex Waldent files exhibit lower resistance to fracture.