The extension of wood to a wider field has been restrained significantly due to its dimensional instability that arises from variation in moisture content, which in turn brings about the risk of cracking, warping or distortion. This work proposed a novel strategy to stabilize wood by means of the in situ construction of a thermotropic shape memory polymer (SMP) inside wood. The cross-linked copolymer network (PMP) with good shape memory behavior was first investigated based on the reaction of methyl methacrylate (MMA) and polyethylene glycol diacrylate (PEGDA) in a water/ethanol solution; then, the PMP was constructed inside wood via vacuum-pressure impregnation and in situ polymerization. The weight gain, volume increment and morphology observations clearly revealed that the PMP was mainly present in wood cell lumens, cell walls and pits. The presence of PMP significantly enhanced the dimensional stability of and reduced the cracks in wood. The desirable shape recovery abilities of PMP under heating-cooling cycles were considered to be the main reasons for wood dimensional stabilization, because it could counteract the internal stress or retard the shrinkage of cell walls once water was evaporated from the wood. This study provided a novel and reliable approach for wood modification.

Microbes naturally inhabit bamboo-based materials in outdoor environments, sequentially contributing to their deterioration. Fungi play a significant role in deterioration, especially in environments with abundant water and favorable temperatures. Alkali treatment is often employed in the pretreatment of round bamboo to change its natural elastic and aesthetic behaviors. However, little research has investigated the structure and dynamics of fungal communities on alkali-treated round bamboo during natural deterioration. In this work, high-throughput sequencing and multiple characterization methods were used to disclose the fungal community succession and characteristic alterations of alkali-treated round bamboo in both roofed and unroofed habitats throughout a 13-week deterioration period. In total, 192 fungal amplicon sequence variants (ASVs) from six phyla were identified. The fungal community richness of roofed bamboo samples declined, whereas that of unroofed bamboo samples increased during deterioration. The phyla Ascomycota and Basidiomycota exhibited dominance during the entire deterioration process in two distinct environments, and the relative abundance of them combined was more than 99%. A distinct shift in fungal communities from Basidiomycota dominant in the early stage to Ascomycota dominant in the late stage was observed, which may be attributed to the increase of moisture and temperature during succession and the effect of alkali treatment. Among all environmental factors, temperature contributed most to the variation in the fungal community. The surface of round bamboo underwent continuous destruction from fungi and environmental factors. The total amount of cell wall components in bamboo epidermis in both roofed and unroofed conditions presented a descending trend. The content of hemicellulose declined sharply by 8.3% and 11.1% under roofed and unroofed environments after 9 weeks of deterioration. In addition, the contact angle was reduced throughout the deterioration process in both roofed and unroofed samples, which might be attributed to wax layer removal and lignin degradation. This study provides theoretical support for the protection of round bamboo under natural weathering.

Bamboo’s mechanical and aesthetic properties are significantly influenced by fungi. However, few studies have been conducted to investigate the structure and dynamics of fungal communities in bamboo during its natural deterioration. In this study, fungal community succession and characteristic variations of round bamboo in roofed and unroofed environments over a period of 13 weeks of deterioration were deciphered using high-throughput sequencing and multiple characterization methods. A total of 459 fungal Operational Taxonomic Units (OTUs) from eight phyla were identified. The fungal community’s richness of roofed bamboo samples showed an increasing trend, whereas that of unroofed bamboo samples presented a declining trend during deterioration. Ascomycota and Basidiomycota were the dominant phyla throughout the deterioration process in two different environments: Basidiomycota was found to be an early colonizer of unroofed bamboo samples. Principal Coordinates Analysis (PCoA) analysis suggested that the deterioration time had a greater impact on fungal community variation compared to the exposure conditions. Redundancy analysis (RDA) further revealed that temperature was a major environmental factor that contributed to the variation in fungal communities. Additionally, the bamboo epidermis presented a descending total amount of cell wall components in both roofed and unroofed conditions. The correlation analysis between the fungal community and relative abundance of three major cell wall components elucidated that Cladosporium was negatively correlated with hemicellulose in roofed samples, whereas they presented a positive correlation with hemicellulose and a negative correlation with lignin in unroofed samples. Furthermore, the contact angle decreased during the deterioration process in the roofed as well as unroofed samples, which could arise from the degradation of lignin. Our findings provide novel insights into the fungal community succession on round bamboo during its natural deterioration and give useful information for round bamboo protection.

Bamboo is a natural and renewable building material but its application has been limited due to the low dimensional stability and poor durability against mold. In this study, monomers of hydroxyethyl methacrylate (HEMA) and N-isopropyl acrylamide (NIPAM) were impregnated in bamboo to facilitate the in situ growth of poly-HEMA and NIPAM (PHN) copolymer. Prior to that, the effects of different reaction conditions, including the molar ratio of HEMA to NIPAM and their concentrations, the amount of initiator (ammonium persulfate, APS) and crosslinking agents (N,N′-Methylenebisacrylamide (MBA), and glutaric dialdehyde (GA)) on the swelling capacity of PHN were optimized. The formation of PHN was confirmed by using Fourier transform infrared spectroscopy and thermogravimetric analysis, which shows the characteristics peaks of both HEMA and NIPAM, and increased pyrolysis and glass transition temperatures, respectively. After impregnation of PHN pre-polymerization formulation to bamboo, it was observed that PHN filled most of the pits in the bamboo cell wall and formed a tight network. Moreover, the dimensional stability of PHN treated bamboo was significantly improved with an anti-swelling efficiency of 49.4% and 41.7%, respectively, after wetting–drying and soaking–drying cycles. A mold infection rate of 13.5% was observed in PHN-treated bamboo as compared to a 100% infected control group after a 30-day mold resistance test. Combined results indicate that in situ polymerization of HEMA and NIPAM in bamboo is a promising method to develop exterior used bamboo products with enhanced dimensional stability and mold resistance.