The effects of welding energy on the mechanical and microstructural characteristics of ultrasonic-welded pure copper plates were investigated. Complex dynamic recrystallization and grain growth occurred inside the weld zone during ultrasonic welding. At a low welding energy, a thin band of straight weld interfaces was observed and had an ultra-fine grain structure. With an increase in welding energy, the weld interface progressively changed from flat to sinusoidal, and eventually turned into a convoluted wavy pattern, bearing similarities to shear instabilities, as observed in fluid dynamics. The lap shear load of the joints initially increased and then remained stable as the welding energy increased. The tensile characteristics of the joints significantly depended on the development of plastic deformation at the interface. The influence of the microstructure on the hardness was also discussed.

The effects of vibration amplitude on the interface reaction and mechanical strength of the Cu/Al joints were systematically investigated in ultrasonic spot welding (USW) experiments. The appropriate vibration amplitude (22.5 μm) was beneficial for obtaining a sound joint. The formation of the continuous intermetallic compounds (IMC) layer accelerated with a higher vibration amplitude. The lap shear tensile strength of the Cu/Al joints decreased when the thickness of the intermetallic layer was greater than 1 μm at various amplitudes. With the increase in welding time, a crack occurred in the copper side owing to the occurrence of the eutectic reaction, $\mathit{\alpha -A}l+\theta \to L$ , at the periphery of the nugget. The remarkable decline of ultrasonic power curves occurred at various amplitude levels upon the formation of a crack in the copper side.

Plasma electrolytic oxidation processing is a novel promising surface modification approach for various materials. However, its large-scale application is still restricted, mainly due to the problem of high energy consumption of the plasma electrolytic oxidation processing. In order to solve this problem, a novel intelligent self-adaptive control technology based on real-time active diagnostics and on the precision adjustment of the process parameters was developed. Both the electrical characteristics of the plasma electrolytic oxidation process and the microstructure of the coating were investigated. During the plasma electrolytic oxidation process, the discharges are maintained in the soft-sparking regime and the coating exhibits a good uniformity and compactness. A total specific energy consumption of 1.8 kW h m⁻² μm⁻¹ was achieved by using such self-adaptive plasma electrolytic oxidation processing on pre-anodized 6061 aluminum alloy samples.

Micro resistance spot welding (MRSW) is an important technology widely used in electronics manufacturing for micro component joining. For the joining of micro enameled wire, quality control is heavily dependent on manual inspection till now. In this paper, a quality monitoring approach based on isolation forest (iForest) is proposed to identify abnormal welds and normal welds. Electrode voltage and welding current of over 110,000 spot welds were collected from a production line. The dynamic resistance and heat input were calculated for all welds and used for feature extraction. A class imbalance problem existed in the collected dataset because abnormal welds were far fewer than normal welds. The anomaly detection model based on iForest was established for the imbalanced data classification after comparison with other methods such as one-class (support vector machine) SVM and local outlier factor. Test results show that the similarity of dynamic resistance profile and heat input compared with the previous ten welds are valid features for detecting a part of the abnormal welds. The iForest model is effective for distinguishing incomplete fusion welds from normal welds with high efficiency. It can assist in the on-line quality monitoring of enameled wire welding process in production.

Micro-arc discharge events and dielectric breakdown of oxide films play an important role in the formation process of plasma electrolytic oxidation coating. Single pulse anodization of micro-electrodes was employed to study the discharge behavior and dielectric breakdown of oxide films deposited on aluminum in an alkaline silicate electrolyte. Voltage and current waveforms of applied pulses were measured and surface morphology of micro-electrodes was characterized from images obtained using scanning electron microscope (SEM). A feasible identification method for the critical breakdown voltage of oxide film was introduced. Different current transients of voltage pulses were obtained, depending on applied pulse voltage and duration. In addition, the active capacitive effect and complex non-linear nature of plasma electrolytic oxidation process is confirmed using dynamic electrical characteristic curves. A good correlation between the pulse parameters and shape of discharge channels was observed. Circular opened pores were found to close with increasing potential and pulse width. Finally, the characteristic parameters of a single discharge event were estimated.