The electrical performance of doped semiconducting polymers is strongly governed by processing methods and underlying thin-film microstructure. We report on the influence of different doping methods (solution versus vapor) on the thermoelectric power factor (PF) of PBTTT molecularly p-doped with F_nTCNQ (n = 2 or 4). The vapor-doped films have more than two orders of magnitude higher electronic conductivity (σ) relative to solution-doped films. On the basis of resonant soft x-ray scattering, vapor-doped samples are shown to have a large orientational correlation length (OCL) (that is, length scale of aligned backbones) that correlates to a high apparent charge carrier mobility (μ). The Seebeck coefficient (α) is largely independent of OCL. This reveals that, unlike σ, leveraging strategies to improve μ have a smaller impact on α. Our best-performing sample with the largest OCL, vapor-doped PBTTT:F₄TCNQ thin film, has a σ of 670 S/cm and an α of 42 μV/K, which translates to a large PF of 120 μW m⁻¹ K⁻². In addition, despite the unfavorable offset for charge transfer, doping by F₂TCNQ also leads to a large PF of 70 μW m⁻¹ K⁻², which reveals the potential utility of weak molecular dopants. Overall, our work introduces important general processing guidelines for the continued development of doped semiconducting polymers for thermoelectrics.

We demonstrate how processing methods affect the thermoelectric properties of thin films of a high mobility semiconducting polymer, PBTTT. Two doping methods were compared: vapor deposition of (tridecafluoro-1,1,2,2-tetrahydrooctyl)trichlorosilane (FTS) or immersion in a solvent containing 4-ethylbenzenesulfonic acid (EBSA). Thermally annealed, thin films doped by FTS deposited from vapor yield a high Seebeck coefficient (α) at high electronic conductivity (σ) and, in turn, a large power factor (PF = α²σ) of ∼100 μW m^–1 K^–2. The FTS-doped films yield α values that are a factor of 2 higher than the EBSA-doped films at comparable high value of σ. A detailed analysis of X-ray scattering experiments indicates that perturbations in the local structure from either dopant are not significant enough to account for the difference in α. Therefore, we postulate that an increase in α arises from the entropic vibrational component of α or changes in scattering of carriers in disordered regions in the film.

Pluripotency, which is defined as a system not fixed as to its developmental potentialities, is typically associated with biology and stem cells. Inspired by this concept, we report synthetic polymers that act as a single “pluripotent” feedstock and can be differentiated into a range of materials that exhibit different mechanical properties, from hard and brittle to soft and extensible. To achieve this, we have exploited dynamic covalent networks that contain labile, dynamic thia-Michael bonds, whose extent of bonding can be thermally modulated and retained through tempering, akin to the process used in metallurgy. In addition, we show that the shape memory behavior of these materials can be tailored through tempering and that these materials can be patterned to spatially control mechanical properties.