The research presented in the current paper was carried out for the experimental steel designed for plate which meets the requirements for grade X100 according to API5L. Physical modeling of the rolling process was carried out using the GLEEBLE 3800 simulator. The tested steel is fine-grained constructional steel for making tubes for gas pipelines with the working pressure higher than 15 MPa. The fine-grained structure guarantees excellent plastic properties as well as high impact toughness. After rolling the steel should obtain the minimal yield point of 690 MPa and tensile strength over 760 MPa.

In order to enhance the quality of plates, various solutions are being implemented, including normalizing rolling, the process of rolling followed by accelerated cooling, as well as new roll gap control systems. The hydraulic positioning of rolls and the working roll bending system can be mentioned here. The implementation of those systems results in increased loads of the rolling stands and working tools, that is the rolls. Another solution aimed at enhancing the cross-sectional and longitudinal shape of rolled plate is the introduction of asymmetric rolling, which consists in the intentional change of the stress and strain state in the roll gap. Asymmetric rolling systems have been successfully implemented in strip cold rolling mills, as well as in sheet hot rolling mills. The paper present results of studies on the effect of roll rotational speed asymmetry and other rolling process parameters on the change in the shape of rolled strip and the change of rolls separating force for the conditions of normalizing rolling of plates in the finishing stand. The variable process parameters were: the roll rotational speed asymmetry factor, av; the strip shape factor, h0/D; and the relative rolling reduction, ε. Working rolls of the diameter equal to 1000 mm and a constant lower working roll rotational speed of n = 50 rpm were assumed for the tests. The asymmetric rolling process was run by varying the rotational speed of the upper roll, which was lower than that of the lower roll. The range of variation of the roll rotational speed factor, av =vd/vg, was 1.01÷1.15. A strip shape factor of h0/D = 0.05÷0.014 was assumed. The range of rolling reductions applied was ε = 0.08÷0.50. The material used for tests was steel of the S355J2G3 grade. For the simulation of the three-dimensional plastic flow of metal in the roll gap during the asymmetric hot rolling of plates, the mathematical model of the FORGE 2008 ® program was used. For the mathematical description of the effect of rolling parameters on the strip curvature and rolls separating force the special multivariable polynomial interpolation was used. This method of tensor interpolation in Borland Builder programming environment was implemented. On the basis of the carried out analysis can be state, that by using the appropriate relative rolling reduction and working roll peripheral speed asymmetry factor for a given feedstock thickness (strip shape ratio) it is possible to completely eliminate the unfavorable phenomenon of strip bending on exit from the roll gap, or to obtain the permissible strip curvature which does not obstructs the free feed of the strip to the next pass or transferring the plate to the accelerated plate cooling stations. Additionally by introducing the asymmetric plate rolling process through differentiating working roll peripheral speeds, depending on the asymmetry factor used, the magnitude of the total roll separating force can be reduced and, at the same time, a smaller elastic deflection of rolling stand elements can be achieved. As a result smaller elastic deflection of the working rolls, smaller dimensional deviations across its width and length finished plate can be obtained.

The requirement for curde oil and natural gas is still increasing. It was observed a growing of interested in the exploration and exploatation of unconventional fuels, including shate gas. There is about 3 to 5 trilion cubic meters resources of that type of gas in Poland. The latest data predicts that in addition to gas in the shale is also petroleum. The development of this branch of mining in our country can cause a significant increase in demand for pipes. The results of basic research of experimental steels for pipe line are presented in this article. Analyse of published materials about steels for pipe line was done. The chemical composition of two types of new steels meeting the requirements for X80 and X100 grade plates according API 5L norm were developed. The heat tratment using dilatometer DIL 805A/D were carried out. The influnce of heat temperature before rolling proces on structure of austenite was defined. The heating schemes were proposed for obtaining a high yield, while not allowing the dissolution of the alloying elements inhibit austenite grain overdevelopment. For samples after tests the structure of primary austenite and the size of former austenite grains were determined. The influence of deformation cinditions on structure were determinated, too. The results obtained from the examinations will be used to develop a technology for rolling sheets of pipelines in the category of X80 and X100 according to the API.

In order to improve the quality of plates, an asymmetric rolling process can be introduced, which will help reduce the total roll separating force and increase plate flatness and decrease thickness deviations along the width and length of rolled strip [1÷.

Physical Simulation of Controlled Rolling and Accelerated Cooling for Ultrafine-Grained Steel Plates: The work shows the possibilities of obtaining ultrafine-grained ferrite-pearlite and ferrite-bainite structures in the process of controlled rolling of sheet metal using immediate accelerated cooling after the final pass. Low-carbon steel without micro-alloy additives was analyzed. The analysis was conducted using the Gleeble 3800 device with Hydrawedge II MCU module which enabled a multiple cycle of fast compression of the material. During the test, 10×15×20 mm rectangular parallelepiped specimens were deformed in flat anvils gaining the flat state of deformation in the zone of compression. Then the influence of the used scheme of deformation, cooling rate, time of break between the last deformation and the beginning of the accelerated cooling was analyzed as well as the temperature at the end of accelerated cooling of the structure and the mechanical properties of the final item.