For the development and optimization of solid-state symmetrical supercapacitors, herein, we propose using carbon-based electrodes and sodium- and lithium-form Aquivion electrolyte membranes, which serve as the separator and electrolyte. Carbon xerogels, synthesized using microwave-assisted sol-gel methodology, with designed and controlled properties were obtained as electrode materials. Commercial activated carbon (YP-50F, “Kuraray Europe” GmbH) was used as the active material for comparison. Notably, the developed solid-state symmetrical supercapacitors provide sufficiently high specific capacitances of 105–110 F g⁻¹ at 0.2 A g⁻¹, along with an energy density of 4.5 Wh kg⁻¹ at 300 W kg⁻¹, and a voltage window of 0–1.2 V in aqueous environments, also demonstrating an excellent cycling stability for up to 10,000 charge/discharge cycles. These results can demonstrate the potential applications of carbon xerogel as the active electrode material and cation exchange membrane as the electrolyte in the development of solid-state supercapacitor devices.

Flexible energy storage devices, such as solid-state supercapacitors, are becoming increasingly attractive due to their characteristics of high electrochemical performance, reliability, light weight, flexibility, absence of electrolyte leakage, high power density, and long lifetime. For the optimization of the solid-state symmetrical supercapacitor proposed in this work, it was employed in sodium and lithium form Aquivion electrolyte membrane, which serves as the separator and electrolyte. As electrode materials, carbon xerogels, synthesized by microwave-assisted sol-gel methodology, with designed and controlled properties were obtained. Commercial activated carbon (YP-50F, 'Kuraray Europe' GmbH) was used for comparison. Specifically, the developed solid-state symmetrical supercapacitors deliver sufficient high specific capacitances of 105−110 F g−1 at 0.2 A g−1, along with an energy density of 4.5 Wh kg−1 at 300 W kg−1, and in a voltage window of 0-1.2 V in an aqueous environments, also demonstrating excellent cycling stability up to 10,000 charge/discharge cycles. These results can demonstrate the potential applications of carbon xerogel as an active electrode material and cation exchange membrane as the electrolyte in the development of solid-state supercapacitor devices

Yttrium-doped barium cerate (BCY15) was used as an anode ceramic matrix for synthesis of the Ni-based cermet anode with application in proton-conducting solid oxide fuel cells (pSOFC). The hydrazine wet-chemical synthesis was developed as an alternative low-cost energy-efficient route that promotes ‘in situ’ introduction of metallic Ni particles in the BCY15 matrix. The focus of this study is a detailed comparative characterization of the nickel state in the Ni/BCY15 cermets obtained in two types of medium, aqueous and anhydrous ethylene glycol environment, performed by a combination of XRD, N₂ physisorption, SEM, EPR, XPS, and electrochemical impedance spectroscopy. Obtained results on the effect of the working medium show that ethylene glycol ensures active Ni cermet preparation with well-dispersed nanoscale metal Ni particles and provides a strong interaction between hydrazine-originating metallic Ni and cerium from the BCY15 matrix. The metallic Ni phase in the pSOFC anode is more stable during reoxidation compared to the Ni cermet prepared by the commercial mechanical mixing procedure. These factors contribute toward improvement of the anode’s electrochemical performance in pSOFC, enhanced stability, and a lower degradation rate during operation.

Yttrium-doped barium cerate (BCY15) was used as ceramic matrix to obtain Ni/BCY15 anode cermet for application in proton-conducting solid oxide fuel cells (pSOFC). Ni/BCY15 cermets were prepared in two different types of medium, namely deionized water (W) and anhydrous ethylene glycol (EG) using wet chemical synthesis by hydrazine. An in-depth analysis of anodic nickel catalyst was made aiming to elucidate the effect of anode tablets’ preparation by high temperature treatment on the resistance of metallic Ni in Ni/BCY15-W and Ni/BCY15-EG anode catalysts. On purpose reoxidation upon high-temperature treatment (1100 °C for 1 h) in air ambience was accomplished. Detailed characterization of reoxidized Ni/BCY15-W-1100 and Ni/BCY15-EG-1100 anode catalysts by means of surface and bulk analysis was performed. XPS, HRTEM, TPR, and impedance spectroscopy measurements experimentally confirmed the presence of residual metallic Ni in the anode catalyst prepared in ethylene glycol medium. These findings were evidence of strong metal Ni network resistance to oxidation in anodic Ni/BCY15-EG. Enhanced resistance of the metal Ni phase contributed to a new microstructure of the Ni/BCY15-EG-1100 anode cermet getting more stable to changes that cause degradation during operation.

Dielectric spectroscopy is a branch of impedance spectroscopy, which is specially tuned for measurements and analyses of the dielectric properties of dielectrics. This article presents experimental results on the dielectric properties of the central membrane in SOFC. The central membrane is made of a monolithic or composite non-polarizable ceramic material, in which a polarizable dielectric - water is located. The studies were conducted in the frequency range from 1 MHz to 0.01 Hz on two types of objects - water in porous composite and porous monolithic functional ceramics. As a result, a new phenomenon was observed - a gigantic increase in the effective capacitance. The phenomenon can be associated with the formation of dipole volume structures induced by an external alternating electric field