This study aims to systematically analyze the effects of different curing temperatures, unit binder content, and the mixture ratios of ground granulated blast-furnace slag and fly ash based on ordinary Portland cement in binders on the development of concrete compressive strength. Particularly, the study evaluates strength characteristics by calculating the maturity equivalent to 28 days of curing at 20 °C. A model based on the relationship between maturity and strength was applied to predict the compressive strength, and the experimental data were analyzed to derive strength coefficients for each variable. The results showed that at a low temperature of 5 °C, the actual strength was lower than the predicted strength, leading to higher error rates. In contrast, at temperatures of 20 °C and 40 °C, the coefficient of determination (R² > 0.90) for the predictive equation was high, and the error rates were reduced to within 10%. The study demonstrates that by combining the maturity method with the strength–maturity relationship, the concrete compressive strength can be effectively predicted under specific curing and binder design conditions.

This study investigated the hardening process of alkali-activated material (AAM) mortar using calcium sulfoalumiante (CSA) expansive additive (CSA EA), which accelerates the initial reactivity of AAMs, and subsequent changes in ultrasonic pulse velocity (UPV). After the AAM mortar was mixed with three different contents of CSA EA, the setting and modulus of elasticity of the mortar at one day of age, which represent curing steps, were measured. In addition, UPV was used to analyze each curing step. The initial and final setting times of the AAM mortar could be predicted by analyzing the UPV results measured for 14 h. In addition, the dynamic modulus of elasticity calculated using the UPV results for 24 h showed a tendency similar to that of the static modulus of elasticity. The test results showed that the use of CSA EA accelerated the setting of the AAM mortar and increased the modulus of elasticity, and these results could be inferred using UPV. The proposed measurement method can be effective in evaluating the properties of a material that accelerates the initial reactivity.

Self-healing cement composites are generally produced by using materials such as inorganic powders, bacteria pellets, and microcapsules. Among them, inorganic powder-type healing materials tend to decrease in healing performance over time because they react relatively quickly. Accordingly, this study encapsulated self-healing inorganic reactive powders in solid capsules (SC) in order to delay their reaction. The capsule surface was coated with a membrane to prevent moisture from permeating it. SC were utilized to provide the self-healing effect to the repair mortar. SC were mixed at three rates (0%, 5%, and 10%) by the binder mass of the repair mortar. The fundamental properties, including rheology, table flow, strength, and length change, and the self-healing performance of the self-healing repair mortar mixes were investigated. It was found that the rheological and mechanical properties of the repair mortar decreased slightly as the amount of SC increased. On the other hand, for a crack width of 0.25 mm and crack inducing age of 28 days, the healing performance of repair mortar specimens containing SC was at least 20 pt% better than that of plain repair mortar after a healing period of 28 days.

Advancements in material science have led to the development of various self-healing concrete technologies. Among these is the use of microcapsule-based self-healing materials. This study evaluated the effects of self-healing microcapsules on the quality and healing properties of mortar. A silicate-based inorganic material mixture was used as the healing material tested with ordinary Portland cement. Accordingly, the effects of microcapsules (MCs) on the rheological, mechanical, and healing properties of mortar were determined. The mixing of MCs reduced the plastic viscosity and yield stress of the cement composite material owing to the particle properties of the MCs. The reduction was in proportion to the mixing ratio. The evaluation results show that the unit water permeability decreased owing to the healing reaction immediately after crack initiation. The healing rate was more than 95% at 7 days of healing age when more than 3% of MCs was mixed. This study provides a reference for the optimal mixing rate of MCs to achieve an ideal concrete healing rate.

This experimental research investigated the applicability of the liquid crystal display (LCD) by-product of the refining process as a sustainable and alternative alkali activator for ground granulated blast-furnace slag (GGBFS) blended cement concrete. Three levels of binder replacement using the industrial by-product, and four water/binder ratios were considered in order to evaluate the effects of the replacement in fresh and hardened properties of the blended concrete. XRD and TG analyses confirmed that the by-product that contains abundant alkali compounds promotes the reactivity of GGBFS. The test results indicated that the incorporation of the by-product results in delayed setting and degraded workability due to the highly porous nature of the by-product, yet shows rapid early-age strength development of the blended concrete as conventional alkaline activators for GGBFS. These characteristics shed light on a simple yet effective and practical means of reusing the industrial by-product as an alternative alkaline activator.

Cement-free concrete has a superior physical performance, such as in its strength and durability, compared to OPC concrete; however, it has the disadvantage of large shrinkage. Large shrinkage can cause cracks due to shrinkage stress in the long term. In this study, a shrinkage reducing agent (SRA) was used to reduce the shrinkage of cement-free mortar; its content was increased from 0.0 to 1.5%. For an SRA content of 1.0%, a calcium sulfoaluminate (CSA) expansive additive (EA) (2.5, 5.0, and 7.5%) was added. To calculate the shrinkage stress of cement-free mortar using the SRA and EA, the compressive strength, elastic modulus, and total and autogenous shrinkage were measured. The unit shrinkage stress of cement-free mortar was obtained by multiplying the elastic modulus by the length change and accumulated to obtain the shrinkage stress acting on the mortar according to the age. The shrinkage stress of cement-free mortar showed different tendencies as the age increased. At early ages, the shrinkage rate of the mortar occupied a large proportion of the shrinkage stress. In the long term, the shrinkage stress was significantly affected by the elastic modulus. As a result, SRA was found to be effective in reducing the shrinkage stress by decreasing both the elastic modulus and shrinkage. However, EA increased the shrinkage stress over the long term due to an increase in the elastic modulus even though it compensated for early-ages shrinkage.