We present the results of obtaining and investigating multiferroic ceramics Pb(Fe_1/2Nb_1/2)O₃ (PFN) and PFN doped by various amounts of Li (PFN:Li). Ceramics have been obtained from oxides by two-step synthesis. For obtained samples the X-ray diffraction patterns, microstructure, DC electric conductivity, the temperature dependencies of dielectric permittivity and dielectric losses, electromechanical properties and hysteresis loops have been investigated. Obtained results have shown that the introduction of Li decreases electric conductivity and improves dielectric and electromechanical parameters important for applications.

This paper presents the results of investigations of the ceramic samples of perovskite type solid solution (Pb_1-xLa_x)(Zr_1-yTi_y)O₃ (PLZT—with x = 0.02, 0.03, 0.06 and 0.10, y = 0.9). Ceramic samples have been obtained from oxides using classical ceramic technology. The main aim of this paper is to compare the energy storage densities calculated from the P-E loops (at frequency of 1Hz) obtained as a result of integrating the area enclosed by E-P curve for tree types of ceramics—ferroelectric (PLZT with x = 0.02), slim-loop antiferroelectric (PLZT with x = 0.6, 0.10) and normal antiferroelectric with double loops (PLZT with x = 0.03).

The results of the investigations on (1 — x)PMN-xPT ceramic samples obtained by sol—gel (SG) technology are presented in this study. In the (1 — x)PMN-xPT samples, the temperature Tm (at which real part of dielectric permittivity reaches its maximum) increases from ~270 K for x = 0 to ~500 K for x = 0.5. At room temperature, the samples with low values of x exhibit relaxor properties, while with increasing x the transition to normal ferroelectric properties takes place. Usually 0.9PMN-0.1PT or 0.925PMN-0.075PT solid solutions are considered as boundary compositions between relaxor and ferroelectric properties at room temperature.This study presents the analysis of X-ray diffraction patterns, fracture microphotographs, electromechanical parameters, and hysteresis loops for ceramics obtained from SG PMN—PT powders densified by the hot pressing method with a composition range, x = 0—0.37.