Carbonization of biomass residues followed by activation has great potential to become a safe process for the production of various carbon materials for various applications. Demand for commercial use of biomass-based carbon materials is growing rapidly in advanced technologies, including in the energy sector, as catalysts, batteries and capacitor electrodes. In this study, carbon materials were synthesized from hardwood using two carbonization methods, followed by activation with H₃PO₄, KOH and NaOH and doping with nitrogen. Their chemical composition, porous structure, thermal stability and structural order of samples were studied. It was shown that, despite the differences, the synthesized carbon materials are active catalysts for oxygen reduction reactions. Among the investigated carbon materials, NaOH-activated samples exhibited the lowest Tafel slope values, of −90.6 and −88.0 mV dec^–1, which are very close to the values of commercial Pt/C at −86.6 mV dec^–1.

This study focuses on fabricating cobalt particles deposited on graphitic carbon nitride (Co/gCN) using annealing, microwave-assisted and hydrothermal syntheses, and their employment in hydrogen and oxygen evolution (HER and OER) reactions. Composition, surface morphology, and structure were examined using inductively coupled plasma optical emission spectroscopy, X-ray photoelectron spectroscopy, and X-ray diffraction. The performance of Co-modified gCN composites for the HER and OER were investigated in an alkaline media (1 M KOH). Compared to the metal-free gCN, the modification of gCN with Co enhances the electrocatalytic activity towards the HER and OER. Additionally, thermal annealing of both Co(NO₃)₂ and melamine at 520 °C for 4 h results in the preparation of an effective bifunctional Co₃O₄/gCN catalyst for the HER with the lower E_onset of −0.24 V, a small overpotential of −294.1 mV at 10 mA cm⁻², and a low Tafel slope of −29.6 mV dec⁻¹ in a 1.0 M KOH solution and for the OER with the onset overpotential of 286.2 mV and overpotential of 422.3 mV to achieve a current density of 10 mA cm⁻² with the Tafel slope of 72.8 mV dec⁻¹.

The perfect strategy for the generation of green and renewable hydrogen (H₂) fuels is the direct electrocatalytic splitting of plentiful seawater rather than scarce freshwater. One of the half-reactions taking place during the electrocatalytic splitting of seawater is oxygen evolution (OER). However, the OER is affected by slow four-electron transfer kinetics as well as competitive chlorine evolution reactions (CERs) in seawater. To overcome the kinematic and competitive barriers of seawater splitting and achieve an excellent overall performance of seawater splitting, we herein report a facile, low-cost, one-step fabrication procedure of 3D structured nickel–manganese (NiMn) coatings using a dynamic hydrogen bubble template (DHBT) technique. The electrocatalytic activities of the thus synthesized catalytic materials for OER in simulated seawater (0.5 M NaCl + 1 M KOH, denoted as SSW) and alkaline natural seawater (natural seawater + 1 M KOH, denoted as ASW) were investigated using linear sweep voltammetry (LSV) at varying temperatures from 25 to 75 °C. Scanning electron microscopy (SEM) and inductively coupled plasma–optical emission spectroscopy (ICP–OES) were used to examine the surface morphology and composition of the prepared catalysts. It was found that the prepared NiMn/Ti-1 catalyst in a plating bath containing a molar ratio of 1:1 Ni²⁺:Mn²⁺ and having the lowest Mn loading of 13.43 µg cm⁻² exhibited quite reasonable activity for OER in Cl⁻ ion rich SSW and ASW. To achieve the benchmark current density of 10 mA cm⁻² in SSW and ASW, the NiMn/Ti-1 electrocatalyst requires overpotentials of 386 and 388 mV, respectively. In addition, this optimal bimetallic electrocatalyst also demonstrated superior long-run stability at 1.81 V (vs. RHE) and 10 mA cm⁻² for 24 h in both working electrolytes. Impressively, the two-electrode electrolyzer—NiMn/Ti-5₍₋₎||NiMn/Ti-1₍₊₎—needs only 1.619 V to deliver 10 mA cm⁻² current density for overall alkaline seawater electrolysis, which is even 0.075 V lower than the noble metal-based electrolyzer (Pt₍₋₎||NiMn/Ti-1₍₊₎).

In this study, a platinum-coated Ni foam catalyst (denoted PtNi/Ni foam) was investigated for the oxidation of the formate reaction (FOR) in an alkaline medium. The catalyst was fabricated via a two-step procedure, which involved an electroless deposition of the Ni layer using sodium hypophosphite as a reducing agent and the subsequent electrodeposition of the platinum layer. The PtNi/Ni foam catalyst demonstrated enhanced electrocatalytic activity for the FOR in an alkaline medium compared to the Ni/Ni foam catalyst and pure Pt electrode. Moreover, the PtNi/Ni foam catalyst promoted the FOR at more negative potentials than the Pt electrode. This contributed to a significant negative shift in the onset potential, indicating the high activity of the catalyst. Notably, in alkaline media with the PtNi/Ni foam catalyst, the FOR proceeds via a direct pathway mechanism without significant accumulation of poisonous carbonaceous species on the PtNi/Ni foam catalyst.

In this study we present an application of wood biomass—alder wood char—as the carbon precursor for the synthesis of novel and sustainable nitrogen-doped activated-carbon-supported nickel nanoparticle catalyst (AWC-Ni-N) for hydrazine oxidation. For comparison, the wood-based carbon material doped with nitrogen only (AWC-N) was also synthesized. Extensive characterization, including SEM, Raman spectroscopy, XPS, and XRD revealed the catalysts’ microstructure and properties. Electrochemical testing demonstrated that the AWC-Ni-N catalyst significantly enhanced the efficiency of the hydrazine oxidation reaction. In addition, direct N₂H₄-H₂O₂ single-fuel-cell tests were conducted using the prepared AWC-N and AWC-Ni-N catalysts as the anodes and cathodes. Peak power densities of up to 10.8 mW cm⁻² were achieved at 25 °C, corresponding to a current density of 27 mA cm⁻² and a cell voltage of 0.4 V when the AWC-Ni-N catalyst was used as both the anode and cathode. Furthermore, the peak power density increased by approximately 1.6 and 2.9 times, respectively, when the operating temperature was raised from 25 °C to 55 °C for the AWC-N and AWC-Ni-N catalysts. Overall, the AWC-N and AWC-Ni-N catalysts demonstrated significant potential as anode and cathode materials in direct N₂H₄-H₂O₂ fuel cells.

AuCeO2/C and Au/C catalysts were obtained by adsorption of AuNPs on the CeO2/C and pure carbon (C) substrates from an Au colloidal solution. It has been found that AuNPs of ca. 50 nm in size were adsorbed on the surfaces of CeO2/C and C; however, electrocatalytic activity of the investigated AuCeO2/C and Au/C catalysts was different. Ethylene glycol oxidation current density values are ca. 3 times higher on the AuCeO2/C catalyst as compared to those of the bare Au/C catalyst. Moreover, the AuCeO2/C catalyst showed more positive onset potentials, as well as higher current in the mixed-kinetic-diffusion region towards the oxygen reduction reaction in an alkaline medium compared to that of the Au/C catalyst.