In this study, a platinum-coated Ni foam catalyst (denoted PtNi/Ni foam) was investigated for the oxidation of the formate reaction (FOR) in an alkaline medium. The catalyst was fabricated via a two-step procedure, which involved an electroless deposition of the Ni layer using sodium hypophosphite as a reducing agent and the subsequent electrodeposition of the platinum layer. The PtNi/Ni foam catalyst demonstrated enhanced electrocatalytic activity for the FOR in an alkaline medium compared to the Ni/Ni foam catalyst and pure Pt electrode. Moreover, the PtNi/Ni foam catalyst promoted the FOR at more negative potentials than the Pt electrode. This contributed to a significant negative shift in the onset potential, indicating the high activity of the catalyst. Notably, in alkaline media with the PtNi/Ni foam catalyst, the FOR proceeds via a direct pathway mechanism without significant accumulation of poisonous carbonaceous species on the PtNi/Ni foam catalyst.

In this study, one-pot microwave-assisted synthesis was used to fabricate the graphene (GR)-supported PtCoM catalysts where M = Mn, Ru, and Mo. The catalysts with the molar ratios of metals Pt:Co:Mn, Pt:Co:Ru, and Pt:Co:Mo equal to 1:3:1, 1:2:2, and 7:2:1, respectively, were prepared. Catalysts were characterized using Transmission Electron Microscopy (TEM). The electrocatalytic activity of the GR-supported PtCoMn, PtCoRu, and PtCoMo catalysts was evaluated toward methanol oxidation in an alkaline medium employing cyclic voltammetry and chrono-techniques. The most efficient electrochemical characteristics demonstrated the PtCoMn/GR catalyst with a current density value of 144.5 mA cm⁻², which was up to 4.8 times higher than that at the PtCoRu(1:2:2)/GR, PtCoMo(7:2:1)/GR, and bare Pt/GR catalysts.

The electrolysis of water is one of low-cost green hydrogen production technologies. The main challenge regarding this technology is designing and developing low-cost and high-activity catalysts. Herein, we present a strategy to fabricate flexible electrocatalysts based on nickel–iron (NiFe) alloy coatings. NiFe coatings were plated on the flexible copper-coated polyimide surface (Cu/PI) using the low-cost and straightforward electroless metal-plating method, with morpholine borane as a reducing agent. It was found that Ni₉₀Fe₁₀, Ni₈₀Fe₂₀, Ni₆₀Fe₄₀, and Ni₃₀Fe₇₀ coatings were deposited on the Cu/PI surface; then, the concentration of Fe²⁺ in the plating solution was 0.5, 1, 5, and 10 mM, respectively. The morphology, structure, and composition of Ni_xFe_y/Cu/PI catalysts have been examined using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), and inductively coupled plasma–optical emission spectroscopy (ICP-OES), whereas their activity has been investigated for hydrogen evolution (HER) and oxygen evolution (OER) reactions in 1 M KOH using linear sweep voltammetry (LSVs). It was found that the Ni₈₀Fe₂₀/Cu/PI catalyst exhibited the lowest overpotential value of −202.7 mV for the HER, obtaining a current density of 10 mA cm⁻² compared to Ni₉₀Fe₁₀/Cu/PI (−211.9 mV), Ni₆₀Fe₄₀/Cu/PI (−276.3 mV), Ni₃₀Fe₇₀/Cu/PI (−278.4 mV), and Ni (−303.4 mV). On the other hand, the lowest OER overpotential (344.7 mV) was observed for the Ni₆₀Fe₄₀/Cu/PI catalyst, obtaining a current density of 10 mA cm⁻² compared to the Ni₃₅Fe₆₅ (369.9 mV), Ni₈₀Fe₂₀ (450.2 mV), and Ni₉₀Fe₁₀ (454.2 mV) coatings, and Ni (532.1 mV). The developed Ni₆₀Fe₄₀/Cu/PI catalyst exhibit a cell potential of 1.85 V at 10 mA cm⁻². The obtained catalysts seem to be suitable flexible catalysts for HER and OER in alkaline media.

A Pt-coated Ni layer supported on a Ni foam catalyst (denoted PtNi/Ni_foam) was investigated for the electro-oxidation of the formic acid (FAO) in acidic media. The prepared PtNi/Ni_foam catalyst was studied as a function of the formic acid (FA) concentration at bare Pt and PtNi/Ni_foam catalysts. The catalytic activity of the PtNi/Ni_foam catalysts, studied on the basis of the ratio of the direct and indirect current peaks (j^d)/(j^nd) for the FAO reaction, showed values approximately 10 times higher compared to those on bare Pt, particularly at low FA concentrations, reflecting the superiority of the former catalysts for the electro-oxidation of FA to CO₂. Ni foams provide a large surface area for the FAO, while synergistic effects between Pt nanoparticles and Ni-oxy species layer on Ni foams contribute significantly to the enhanced electro-oxidation of FA via the direct pathway, making it almost equal to the indirect pathway, particularly at low FA concentrations.

The Ni-Fe coatings modified with AuNPs were deposited on the flexible copper-coated polyimide (Cu/PI) surface using electroless metal plating, while the galvanic displacement technique was applied to modify the surface of NiFe coatings by a small content of AuNPs in the range of 16.5 µg_Au cm⁻². AuNPs of a few nanometers in size were deposited on the NiFe/Cu/PI surface by immersing it in a solution containing AuCl₄⁻ ions. The electrooxidation of sodium borohydride was evaluated in a 1 M NaOH solution containing 0.05 M of sodium borohydride using cyclic voltammetry, chronoamperometry, and chronopotentiometry. In addition, the performance and stability of the NiFe/Cu/PI and AuNPs-NiFe/Cu/PI catalysts were evaluated for potential use in a direct NaBH₄-H₂O₂ fuel cell. The NiFe coating modified with AuNPs demonstrated significantly higher electrocatalytic activity towards the oxidation of sodium borohydride as compared to bare Au or unmodified NiFe/Cu/PI. Furthermore, it exhibited a superior power density of 89.7 mW cm⁻² at room temperature and operational stability under alkaline conditions, while the NiFe anode exhibited 73.1 mW cm⁻². These results suggest that the AuNPs-modified NiFe coating has great potential as a material for use in direct borohydride fuel cells (DBFCs) applications involving the oxidation of sodium borohydride.

Pt-coated Ni layer supported on Ni foam catalyst (denoted PtNi/Nifoam) was investigated for the oxidation of the formic acid (FAO) in acidic media. The prepared PtNi/Ni foam catalyst was studied as a function of the formic acid (FA) concentration at bare Pt and PtNi/Nifoam catalysts. The catalytic activity of the PtNi/Nifoam catalysts, studied on the basis of the ratio of the direct and indirect current peaks (jd)/(jnd) for the FAO reaction, showed values about 10 times higher compared to those on bare Pt, particularly at a low formic acid concentrations, reflecting the superiority of the former catalysts for the oxidation of FA to CO2. Ni foams provide a large surface area for the FOR while synergistic effects between Pt nanoparticles and Ni-oxy species layer on Ni foams contribute significantly to the enhanced oxidation of FA via the direct pathway, making it almost equal to the indirect pathway, particularly at low formic acid concentrations.