This review is dedicated to self-healing silicone materials, which can partially or entirely restore their original characteristics after mechanical or electrical damage is caused to them, such as formed (micro)cracks, scratches, and cuts. The concept of self-healing materials originated from biomaterials (living tissues) capable of self-healing and regeneration of their functions (plants, human skin and bones, etc.). Silicones are ones of the most promising polymer matrixes to create self-healing materials. Self-healing silicones allow an increase of the service life and durability of materials and devices based on them. In this review, we provide a critical analysis of the current existing types of self-healing silicone materials and their functional properties, which can be used in biomedicine, optoelectronics, nanotechnology, additive manufacturing, soft robotics, skin-inspired electronics, protection of surfaces, etc.

In this work, a set of analytical techniques, including scanning electron microscopy (SEM), Raman scattering spectroscopy, X-ray photoelectron spectroscopy (XPS), energy-dispersive X-ray microanalysis (EDX) and cyclic voltammetry (CV), were used to study the impact of high-energy He⁺ ion irradiation on the structural and electrochemical characteristics of sulfur-containing multi-walled carbon nanotubes (S-MWCNTs) placed on a titanium substrate. The results indicate that the ion beam treatment of the S-MWCNT system led to an increase in the level of imperfections on the surface structures of the nanotubes due to the formation of point defects on their outer walls and the appearance of oxygen-containing functional groups, including SO_x groups, near these defects. At the same time, a significant increase in the sulfur concentration (by 6.4 times) was observed on the surface of the S-MWCNTs compared to the surface of unirradiated nanotubes. This was due to the redeposition of sulfur atoms near the point defects under the action of the ion beam, followed by the subsequent formation of direct S–C chemical bonds. Electrochemical studies demonstrated that the irradiated S-MWCNTs/Ti system exhibit enhanced catalytic activity, with improved oxygen reduction reaction (ORR) performance and a substantial increase in anodic current during the oxidation reaction of hydrogen peroxide under alkaline conditions, highlighting their potential for advanced electrocatalytic applications.

Polysiloxanes are unique polymers used in medicine and materials science and are ideal for various modifications. Classic functionalization methods involve a covalent approach, but finer tuning of the properties of the final polymers can also be achieved through sub-sequent noncovalent modifications. This study introduces a fundamentally new approach to polysiloxane functionalization by incorporating cooperative noncovalent interaction centers: selenium-based chalcogen bonding donors and polyfluoroaromatic π-hole acceptors into a single polymer platform. We developed an efficient nucleophilic substitution strategy using poly((3-chloropropyl)methylsiloxane) as a platform for introducing Se-containing groups with polyfluoroaromatic substituents. Three synthetic approaches were evaluated; only direct modification of Cl-PMS-2 proved successful, avoiding catalyst poisoning and crosslinking issues. The optimized methodology utilizes mild conditions and achieved high substitution degrees (74–98%) with isolated yields of 60–79%. Comprehensive characterization using ¹H, ¹³C, ¹⁹F, ⁷⁷Se, and ²⁹Si NMR, TGA, and contact angle measurements revealed significantly enhanced properties. Modified polysiloxanes demonstrated improved thermal stability (up to 37 °C higher decomposition temperatures, 50–60 °C shifts in DTG maxima) and increased hydrophobicity (water contact angles from 69° to 102°). These systems potentially enable chalcogen bonding and arene–perfluoroarene interactions, providing foundations for materials with applications in biomedicine, electronics, and protective coatings. This dual-functionality approach opens pathways toward adaptive materials whose properties can be tuned through supramolecular modification while maintaining the inherent advantages of polysiloxane platforms—flexibility, biocompatibility, and chemical inertness.

This study investigates the electrochemical degradation mechanisms of nickel–salen (NiSalen) polymers, with a focus on improving the material’s stability in supercapacitor applications. We analyzed the effects of steric hindrance near the nickel center by incorporating different bulky substituents into NiSalen complexes, aiming to mitigate water-induced degradation. Electrochemical performance was assessed using cyclic voltammetry, operando conductance, and impedance measurements, while X-ray photoelectron spectroscopy (XPS) provided insights into molecular degradation pathways. The results revealed that increased steric hindrance from methyl groups significantly reduced the degradation rate, particularly in water-containing electrolytes, by hindering water coordination to the Ni center. Among the studied polymers, the highly substituted poly[Ni(Saltmen)] exhibited superior stability with minimal capacity loss. Density functional theory (DFT) calculations further supported that steric protection around the Ni atom effectively lowers the probability of water coordination. These findings suggest that sterically enhanced NiSalen polymers may offer a promising path toward durable supercapacitor electrodes, highlighting the route of molecular engineering to enhance material stability.