Controlling grain size in polycrystalline nickel base superalloy is vital for obtaining required mechanical properties. Typically, a uniform and fine grain size is required throughout forging process to realize the superplastic deformation. Strain amount occupied a dominant position in manipulating the dynamic recrystallization (DRX) process and regulating the grain size of the alloy during hot forging. In this article, the high-throughput double cone specimen was introduced to yield wide-range strain in a single sample. Continuous variations of effective strain ranging from 0.23 to 1.65 across the whole sample were achieved after reaching a height reduction of 70%. Grain size is measured to be decreased from the edge to the center of specimen with increase of effective strain. Small misorientation tended to generate near the grain boundaries, which was manifested as piled-up dislocation in micromechanics. After the dislocation density reached a critical value, DRX progress would be initiated at higher deformation region, leading to the refinement of grain size. During this process, the transformations from low angle grain boundaries (LAGBs) to high angle grain boundaries (HAGBs) and from subgrains to DRX grains are found to occur. After the accomplishment of DRX progress, the neonatal grains are presented as having similar orientation inside the grain boundary.

In this research, the effect of two different per centages of silicon, i.e. 0.08 and 0.3 wt-%, on microstructure and stress rupture life of a Ni-based superalloy was investigated. The results showed that the fraction of eutectic increased from 1.86 to 3.55% with increasing Si content and a higher fraction of eutectic was found on grain boundaries in high Si-bearing alloy. Upon stress rupture at 975°C/225 MPa, cracking initiates and propagates along Laves phases in 0.3 wt-% Si alloy, causing shorter lifetime comparing to that of 0.08 wt-% Si. The microscopic examination uncovered that Si prefers to segregate towards liquid and γ phase, which can explain different rupture lifetimes of two groups of Si-bearing alloys.

The consolidation of metal powders is a complex thermomechanical process, and the temperature has a significant effect on the density distribution in the compact. The consolidation process of metal powders with an average particle size of 10 μm, 25 μm, and 50 μm under hot isostatic pressure was simulated by finite element modeling. The distribution and evolution of the relative density after being hot isostatic pressing (HIP) under 1050 °C/130 MPa/4 h, 1150 °C/130 MPa/4 h, and 1250 °C/130 MPa/4 h conditions were simulated, respectively. The experimental data of HIP at 1050 °C/130 MPa/4 h were used to verify the modeling results via the geometric change in the container. The relative density difference between the simulated results and the experimental results at different positions was less than 2%. This methodology called “modeling prediction, experimental validation” can accelerate experimental discovery in an economic manner.

The electrochemical behaviors of the Ni-base superalloy CMSX-4 were carried out in 3.5 wt.% NaCl solution using electrochemical technique. The electrochemical corrosion process was divided into four stages, and reactions at the alloy surface and corrosion morphology at each stage were analyzed. The passivity mechanism at the stable passivation stage and the occurrence of pitting corrosion at the transpassivation state were discussed especially. The corrosion parameters including E_corr, E_pass, i_pass and E_pit were compared at different temperatures to reveal the relationship between the temperature and the corrosion resistance properties. The corrosion products were investigated by the aid of X-Ray Diffraction (XRD) and Energy Dispersive Spectroscopy (EDS). By designing different preoxidation procedures, the corrosion mechanism of oxide scales was analyzed for the preoxidized samples.

Solidification experiments in two opposite directions were conducted to investigate the buoyancy effect on freckle formation during directional solidification in single-crystal superalloy castings. During conventional upward solidification with the superalloy CMSX-4, severe freckles were observed in castings of various geometries. By reversing the solidification direction from upward to downward, freckle-free castings could be obtained. To visually verify the effect of the solidification direction, an in situ observation experiment by varying the solidification direction was performed using a Ga-In alloy. In the upward solidification process, strong solutal convection was visually observed due to the decrease in the density of the interdendritic liquid. Conversely, a stable condition without visible flow was established during downward solidification, due to the stable state of the top-light, bottom-heavy liquid system. A new Rayleigh-number model was successfully applied to characterize the freckle features in superalloy cluster castings. When the solidification direction was reversed from upward to downward, the driving force for solutal convection was suppressed, leading to the complete elimination of freckle formation in single-crystal superalloy castings.