This study describes the synthesis of an innovative nanomaterial (patent application number BR 1020210000317) composed of cobalt ferrite functionalized in niobium pentoxide CoFe₂O₄@Nb₅O₂ (CFNb), synthesized via green synthesis using tangerine peel extract. The material emphasizes the combination of a magnetic material (which allows for easy recovery after application) with niobium pentoxide (a metal which is abundant in Brazil). CFNb was applied as a catalyst for the paracetamol (PCT) degradation by photocatalysis. The new materials were characterized through surface and pore analysis (S_BET, S_EXT, S_mic, V_mic, and V_TOTAL), photoacoustic spectroscopy (PAS), zero charge point (pH_PZC, scanning electron microscopy (SEM/EDS), and X-ray diffraction (XRD). The reaction parameters studied included pH and catalyst concentration. The results indicated that the CFNb nanocatalysts were efficient in the paracetamol degradation, presenting better results in conditions of low pH (close to 2) and low catalyst concentration under irradiation of the 250 W mercury vapor lamp (greater than 28 mW·cm⁻²) at 60 min of reaction.

In the present work, the performance of Ag/ZnO/CoFe2O4 magnetic photocatalysts in the photocatalytic degradation of ibuprofen (IBP) was evaluated. This study considered the use of pure Ag/ZnO (5% Ag) and also the use of the Ag/ZnO/CoFe2O4 magnetic catalysts containing different amounts (5, 10 and 15% wt) of cobalt ferrite (CoFe2O4). The catalysts were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and photoacoustic spectroscopy. To carry out the photocatalytic degradation reaction, different concentrations of the ibuprofen contaminant solution (10, 20 and 30 ppm) and different concentrations of photocatalyst were tested (0.3 g L−1, 0.5 g L−1 and 1.0 g L−1). The reaction parameters studied were: IBP concentration, catalyst concentration, adsorption and photolysis, influence of the matrix, radiation source (solar and artificial) and the effect of organic additive. At the end of the photocatalytic tests, the best operating conditions were defined. Considering the obtained results of degradation efficiency and magnetic separation, the optimal parameters selected to proceed with the other tests of the study were: ibuprofen solution concentration 10 ppm, Ag/ZnO/CoFe2O4 (5%) catalyst at a concentration of 0.3 g L−1 and pH 4.5 of the reaction medium. The results indicated the feasibility of magnetic separation of the synthesized catalysts. A long duration test indicated that the catalyst exhibits stability throughout the degradation reaction, as more than 80% of IBP was degraded after 300 minutes. The photocatalytic activity was directly affected by the ferrite load. The higher the nominal load of ferrite, the lower the performance in IBP degradation. It was also observed that the smallest amount of ferrite studied was enough for the catalyst to be recovered and reused. The adsorption and photolysis tests did not show significant results in the IBP degradation. In addition, it was possible to verify that the aqueous matrix, the use of solar radiation and the addition of additive (acid formic) were interfered directly in the process. The catalyst reuse tests indicated that it can be recovered and reused at least three times without considerable catalytic activity loss.