Developing highly efficient and durable hydrogen evolution reaction (HER) electrocatalysts is crucial for addressing the energy and environmental challenges. Among the 2D-layered chalcogenides, MoSe₂ possesses superior features for HER catalysis. The van der Waals attractions and high surface energy, however, stack the MoSe₂ layers, resulting in a loss of edge active catalytic sites. In addition, MoSe₂ suffers from low intrinsic conductivity and weak electrical contact with active sites. To overcome the issues, this work presents a novel approach, wherein the in situ incorporated diethylene glycol solvent into the interlayers of MoSe₂ during synthesis when treated thermally in an inert atmosphere at 600 °C transformed into graphene (Gr). This widened the interlayer spacing of MoSe₂, thereby exposing more HER active edge sites with high conductivity offered by the incorporated Gr. The resulting MoSe₂-Gr composite exhibited a significantly enhanced HER catalytic activity compared to the pristine MoSe₂ in an acidic medium and demonstrated a superior HER catalytic activity compared to the state-of-the-art Pt/C catalyst, particularly at a high current density beyond ca. 55 mA cm⁻². Additionally, the MoSe₂-Gr catalyst demonstrated long-term electrochemical stability during HER. This work, thus, presents a facile and novel approach for obtaining an efficient MoSe₂ electrocatalyst applicable in green hydrogen production.

The first-ever demonstration of Ni ₇ S ₆ /NF-based electrolyzer with sugar or orange-juice as active electrolyte for an alternative anodic oxidation reaction in water-electrolysis and achieving a higher rate of green-hydrogen at a lower cell voltage.

After substituting some Co³⁺ ions with Mn³⁺ ions in the Co₃O₄ spinel crystal lattice, the resulting Mn_0.21Co_2.79O₄ nanoneedles demonstrate enhanced electrocatalysis in alkaline water oxidation.