A green synthetic route for the production of silver nanoparticles (AgNPs) using five different aqueous plant extracts, namely, Berberis vulgaris, Brassica nigra, Capsella bursa-pastoris, Lavandula angustifolia and Origanum vulgare, was investigated in this study. The present work demonstrates the influence of plant extract composition (antioxidant and total phenolic content) on the size and morphology of the produced AgNPs. The biosynthetic procedure was rapid and simple and was easily monitored via colour changes and ultraviolet and visible (UV-Vis) spectroscopy. Subsequently, measurement of zeta potential (ZP), photon cross-correlation spectroscopy (PCCS), X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and selected area electron diffraction (SAED) analysis were employed to characterise the as-synthesised nanoparticles. The XRD investigation confirmed the presence of Ag⁰ in the nanoparticles, and interactions between the bioactive compounds of the plants and the produced AgNPs were evident in the FTIR spectra. TEM indicated that the nanoparticles exhibited a bimodal size distribution, with the smaller particles being spherical and the larger having a truncated octahedron shape. In addition, the antimicrobial activity of the AgNPs was tested against five bacterial strains. All synthesised nanoparticles exhibited enhanced antimicrobial activity at a precursor concentration of 5 mM compared to the control substance, gentamicin sulphate, with the best results observed for AgNPs prepared with B. nigra and L. angustifolia extracts.

This study shows mechanochemical synthesis as an alternative method to the traditional green synthesis of silver nanoparticles in a comparative manner by comparing the products obtained using both methodologies and different characterization methods. As a silver precursor, the most commonly used silver nitrate was applied and the easily accessible lavender (Lavandula angustofolia L.) plant was used as a reducing agent. Both syntheses were performed using 7 different lavender:AgNO₃ mass ratios. The synthesis time was limited to 8 and 15 min in the case of green and mechanochemical synthesis, respectively, although a significant amount of unreacted silver nitrate was detected in both crude reaction mixtures at low lavender:AgNO₃ ratios. This finding is of particular interest mainly for green synthesis, as the potential presence of silver nitrate in the produced nanosuspension is often overlooked. Unreacted AgNO₃ has been removed from the mechanochemically synthesized samples by washing. The nanocrystalline character of the products has been confirmed by both X-ray diffraction (Rietveld refinement) and transmission electron microscopy. The latter has shown bimodal size distribution with larger particles in tens of nanometers and the smaller ones below 10 nm in size. In the case of green synthesis, the used lavender:AgNO₃ ratio was found to have a decisive role on the crystallite size. Silver chloride has been detected as a side-product, mainly at high lavender:AgNO₃ ratios. Both products have shown a strong antibacterial activity, being higher in the case of green synthesis, but this can be ascribed to the presence of unreacted AgNO₃. Thus, one-step mechanochemical synthesis (without the need to prepare extract and performing the synthesis as separate steps) can be applied as a sustainable alternative to the traditional green synthesis of Ag nanoparticles using plants.