Symmetric supercapacitors are fabricated by carbon nanofibers (CNF) and activated carbon (AC) using similar proportions of 7 wt% polyvinylidene fluoride (PVDF) polymer binder in an aqueous electrolyte. In this study, a comparison of porous texture and electrochemical performances between CNFs and AC based supercapacitors was carried out. Electrodes were assembled in the cell without a current collector. The prepared electrodes of CNFs and AC present Brunauer-Emmett-Teller (BET) surface area of 83 and 1042 m2/g, respectively. The dominant pore structure for CNFs is mesoporous while for AC is micropore. The results showed that AC provided higher specific capacitance retention up to very fast scan rate of 500 mV/s. AC carbon had a specific capacitance of 334 F/g, and CNFs had 52 F/g at scan rate 5 mV/s in aqueous solution. Also, the results indicate the superior conductivity of CNFs in contrast to AC counterparts. The measured equivalent series resistance (ESR) showed a very small value for CNFs (0.28 Ω) in comparison to AC that has an ESR resistance of (3.72 Ω). Moreover, CNF delivered higher specific power (1860 W/kg) than that for AC (450 W/kg). On the other hand, AC gave higher specific energy (18.1 Wh/kg) than that for CNFs (2 Wh/kg).This indicates that the AC is good for energy applications. Whereas, CNF is good for power application. Indeed, the higher surface area will lead to higher specific capacitance and hence higher energy density for AC. For CNF, lower ESR is responsible for having higher power density. Both CNF and AC supercapacitor exhibit an excellent charge-discharge stability up to 2500 cycles.

Structural energy storage systems offer both load bearing and electrochemical energy storage capabilities in a single multifunctional platform. They are emerging technologies for modern air and ground transportation vehicles, promising considerable mass and volume savings over traditional systems. To this end, carbon fibre reinforced composites have attracted interest for structural supercapacitors (SS), emanating principally from their similar laminate design. However, carbon fibre (CF) electrodes suffer from poor electrochemical storage performance. To tackle this deficiency carbon fiber electrodes were modified with a 3D network of radially grown graphene nanoflakes (GNFs) to enhance their degree of graphitization and active surface area. We show that the GNF surface morphology offers a ~9 times increase in specific capacitance (C_sp) of CF structural supercapacitor. Moreover chemical activation of the GNF/CF hybrid electrodes by urea, induces a further improvement on C_sp by ~14 times, while almost maintaining the elastic modulus of the control CF based device. It has been established that the high specific capacitance stems from the high electro-active edge-dominated nitrogen-moieties and enhanced electrical conductivity induced by urea activation. Overall, the urea-activated hybrid electrodes offer a ~12 fold increase in energy and power densities, compared to CF control structural supercapacitor devices. These findings provide important knowledge for the design of next-generation multifunctional energy storage electrodes by highlighting the importance of interfacial nanoengineering.

Multiwall carbon nanotubes grown by plasma enhanced chemical vapour deposition were functionalized by H(2)O plasma treatment. Through a controlled functionalization process of the carbon nanotubes (CNTs) we were able to modify and tune their chemical reactivity, expanding the range of potential applications in the field of energy and environment. In particular, different oxygen groups were attached to the surfaces of the nanotubes (e.g. carboxyl, hydroxyl and carbonyl), which changed their physicochemical properties. In order to optimize the main operational parameters of the H(2)O plasma treatment, pressure and power, a Box-Wilson experimental design was adopted. Analysis of the morphology, electrochemical properties and functional groups attached to the surfaces of the CNTs allowed us to determine which treatment conditions were suitable for different applications. After water plasma treatment the specific capacitance of the nanotubes increased from 23 up to 68 F g(-1) at a scan rate of 10 mV s(-1).

The need for 2D vertical graphene nanosheets (VGNs) is driven by its great potential in diverse energy, electronics, and sensor applications, wherein many cases a low-temperature synthesis is preferred due to requirements of the manufacturing process. Unfortunately, most of today’s known methods, including plasma, require either relatively high temperatures or high plasma powers. Herein, we report on a controllable synthesis of VGNs at a pushed down low-temperature boundary for synthesis, the low temperatures (450 °C) and low plasma powers (30 W) using capacitively coupled plasma (CCP) driven by radio-frequency power at 13.56 MHz. The strategies implemented also include unrevealing the role of Nickel (Ni) catalyst thin film on the substrates (Si/Al). It was found that the Ni catalyst on Si/Al initiates the nucleation/growth of VGNs at 450 °C in comparison to the substrates without Ni catalyst. With increasing temperature, the graphene nanosheets become bigger in size, well-structured and well separated. The role of Ni catalysts is hence to boost the growth rate, density, and quality of the growing VGNs. Furthermore, this CCP method can be used to synthesize VGNs at the lowest temperatures possible so far on a variety of substrates and provide new opportunities in the practical application of VGNs.