The creation of supercapacitors with superior energy density and power capabilities is critical for advanced energy storage solutions. Ionic liquid electrolytes offer a promising alternative in this respect. However, improving their cycle stability and efficiency is a complex task requiring extensive research and significant effort. The high viscosity of ionic liquids (ILs) limits their lifetime, but this can be mitigated by increasing the temperature or adding solvents. In this research, the electrochemical performance of symmetric activated carbon supercapacitors with 1-Ethyl-3-methylimidazolium tetrafluoroborate (EMIMBF₄) and different ratios of acetonitrile (ACN) as electrolytes were investigated. Long-term galvanostatic charge/discharge tests, impedance studies, and cyclic voltammetry were performed at temperatures between 24 to 60 °C. The addition of ACN to the ionic liquid increased electrochemical stability and reduced internal resistance, with the best performance observed at a 1:2 volume ratio of EMIMBF₄ to ACN. This supercapacitor exhibited 87% cyclic stability after 5000 charge/discharge cycles in the voltage range of 0.05–2.8 V and a current rate of 1 Ag⁻¹. It also achieved an energy density of 23 Whkg⁻¹ and a power density of 748 Wkg⁻¹. The supercapacitors were stable at elevated temperatures up to 60 °C, showing no degradation after operation under various thermal conditions.

Thermally treated caffeine doped active carbon (Caffeine-Norit) is studied as a catalyst for the oxygen reduction reaction (ORR) with application in metal-air systems with neutral aqueous electrolytes. Catalytic activity is characterized by polarization curves and Tafel plots and the results are compared with 5% Platinum (5% Pt-Norit) and 4% Silver (4% Ag-Norit) catalysts. The Tafel slopes of all three catalysts are equal, the activity of Ag-Norit being somewhat lower then both Caffeine-Norit and Pt-Norit. The polarization curves are also comparable, especially in the low current density region. The increase of overpotential for the Caffeine-Norit at current density higher than 50 mA cm ⁻² is due to accumulation of H ₂ O ₂ in the catalyst layer. This was demonstrated by a simple method for detection of peroxides in neutral electrolytes based on indigo carmine indicator. The discharge curves of Caffeine-Norit in 4 M NaCl electrolyte at 10 mA cm ⁻² display a plateau at potential of −320 mV vs Ag/AgCl (1.23 V vs MA8M magnesium alloy).