Strength properties of annealed austenitic stainless steels are relatively low and therefore improvements are desired for constructional applications. The reversion of deformation induced martensite to fine-grained austenite has been found to be an efficient method to increase significantly the yield strength of metastable austenitic stainless steels without impairing much their ductility. Research has been conducted during thirty years in many research groups so that the features of the reversion process and enhanced properties are reported in numerous papers. This review covers the main variables and phenomena during the reversion processing and lists the static and dynamic mechanical properties obtained in laboratory experiments, highlighting them to exceed those of temper rolled sheets. Moreover, formability, weldability and corrosion resistant aspects are discussed and finally the advantage of refined grain structure for medical applications is stated. The reversion process has been utilized industrially in a very limited extent, but apparently, it could provide a feasible processing route for strengthened austenitic stainless steels.

High-pressure torsion (HPT) processing was applied to cast pure magnesium, and the effects of the deformation on the microstructure, hardness, tensile properties and corrosion resistance were evaluated. The microstructures of the processed samples were examined by electron backscatter diffraction, and the mechanical properties were determined by Vickers hardness and tensile testing. The corrosion resistance was studied using electrochemical impedance spectroscopy in a 3.5% NaCl solution. The results show that HPT processing effectively refines the grain size of Mg from millimeters in the cast structure to a few micrometers after processing and also creates a basal texture on the surface. It was found that one or five turns of HPT produced no significant difference in the grain size of the processed Mg and the hardness was a maximum after one turn due to recovery in some grains. Measurements showed that the yield strength of the cast Mg increased by about seven times whereas the corrosion resistance was not significantly affected by the HPT processing.