Strength properties of annealed austenitic stainless steels are relatively low and therefore improvements are desired for constructional applications. The reversion of deformation induced martensite to fine-grained austenite has been found to be an efficient method to increase significantly the yield strength of metastable austenitic stainless steels without impairing much their ductility. Research has been conducted during thirty years in many research groups so that the features of the reversion process and enhanced properties are reported in numerous papers. This review covers the main variables and phenomena during the reversion processing and lists the static and dynamic mechanical properties obtained in laboratory experiments, highlighting them to exceed those of temper rolled sheets. Moreover, formability, weldability and corrosion resistant aspects are discussed and finally the advantage of refined grain structure for medical applications is stated. The reversion process has been utilized industrially in a very limited extent, but apparently, it could provide a feasible processing route for strengthened austenitic stainless steels.

Solid-state welding (SSW) is a relatively new technique, and ongoing research is being performed to fulfill new design demands, deal with contemporary material advancements, and overcome welding defects associated with traditional welding techniques. This work provides an in-depth examination of the advancements in the solid-state welding of steels through diffusion bonding (DB) and friction stir welding (FSW). Considerable attention was given to DB of steel, which overcame the difficulties of segregation, cracking, and distortion stresses that are usually formed in liquid-phase welding techniques. The defects that affected DB included two types: two-dimensional defects of a metallic lattice, i.e., phases and grain boundaries, and three-dimensional defects, i.e., precipitation. FSW, on the other hand, was distinguishable by the use of relatively low heat input when compared to fusion welding processes such as tungsten inert gas (TIG), resulting in the formation of a limited heat-affected zone. Moreover, fine grain structures were formed in the FSW interface because of the stirring tool’s severe plastic deformation, which positively affected the strength, ductility, and toughness of the FSW joints. For instance, higher strength and ductility were reported in joints produced by FSW than in those produced by TIG. Nevertheless, the HAZ width of the specimens welded by FSW was approximately half the value of the HAZ width of the specimens welded by TIG. Some defects associated with FSW related to the diffusion of elements, such as C/Cr atoms, through the weld zone, which affected the local chemical composition due to the formation of rich/depleted regions of the diffused atoms. Moreover, the lack-of-fill defect may exist when inappropriate welding conditions are implemented. On the other hand, the stirring tool was subjected to extensive wear because of the high hardness values, which negatively affected the economical usage of the FSW process. A summary of the results is presented, along with recommendations for future studies aimed at addressing existing difficulties and advancing the solid-state technology for steel.

High-pressure torsion (HPT) processing was applied to cast pure magnesium, and the effects of the deformation on the microstructure, hardness, tensile properties and corrosion resistance were evaluated. The microstructures of the processed samples were examined by electron backscatter diffraction, and the mechanical properties were determined by Vickers hardness and tensile testing. The corrosion resistance was studied using electrochemical impedance spectroscopy in a 3.5% NaCl solution. The results show that HPT processing effectively refines the grain size of Mg from millimeters in the cast structure to a few micrometers after processing and also creates a basal texture on the surface. It was found that one or five turns of HPT produced no significant difference in the grain size of the processed Mg and the hardness was a maximum after one turn due to recovery in some grains. Measurements showed that the yield strength of the cast Mg increased by about seven times whereas the corrosion resistance was not significantly affected by the HPT processing.