Agricultural mechanization is crucial in enhancing production efficiency, alleviating labor demands, reducing costs, improving agricultural product quality, and promoting sustainable development. However, wear and tear are inevitable when using agricultural machinery. The failure of critical wear-resistant parts is responsible for over 50% of rural machinery breakdowns. For instance, a domestic combine harvester typically only operates trouble-free for 20 to 30 h, and the service life of a rotary plow knife is approximately 80 h. Investigating the wear performance of key farm machinery components reinforces machinery design and maintenance strategies, extends machinery lifespans, enhances agricultural production efficiency, and advances agrarian sustainability. This paper provides a comprehensive overview of the latest research on the wear resistance of crucial agricultural machinery components. It delves into the factors influencing the wear resistance of these components and explores current effective measures to address wear-related issues. Additionally, it also summarizes the challenges and opportunities in researching the wear performance of key components in agricultural machinery and future development directions.

The effect and mechanism of grain sizes on the tribological behavior of CoCrFeMnNi high entropy alloy (HEA) were studied by friction experiments and wear morphology analysis. Under normal low load and low sliding speed, the primary wear mechanism of the HEA samples is adhesive wear. With the increase in sliding speed, the wear mechanisms of the samples are adhesive wear and oxidation wear. The oxide layer formed under the action of friction heat of the coarse grain (CG) sample is easy to break due to the softening of the CG. With the increase of normal load and sliding speed, the wear mechanisms of the HEA samples are mainly adhesive wear, oxidation wear, and plastic deformation. The oxide layer of CG sample has many cracks, and the worn surface also has plastic deformation, which leads to the increase of friction coefficient and specific wear rate and the decrease of wear resistance. Therefore, the fine grain size HEA sample has better wear resistance than the CG sample due to its high surface strength.

Compared with the traditional lattice structure, the triply periodic minimal surface (TPMS) structure can avoid stress concentration effectively. Here, it is promising in the fields of lightweight and energy absorption. However, the number of structural parameters and mechanical properties of the TPMS structure is plentiful, and the relationship between them is unclassified. In this paper, for the first time, a unified mathematical model was proposed to establish the relationship between TPMS structural design parameters and mechanical properties. Fifteen primitive models were designed by changing the structural parameters (level-set value C and thickness T) and manufacturing by selective laser melting. The geometric defects and surface quality of the structures were explored by optical microscope and scanning electron microscopy (SEM). The mechanical properties were investigated by quasi-static compression test and finite element simulation. The influence of building direction on structural mechanical behavior (failure mode, stress-strain curve) was studied. The real mechanical properties (Young’s modulus and plateau stress) of the structure could be predicted according to different C and T combinations. Finally, the energy absorption characteristics were explored. The results showed that when the C value is 0.6 in the range of 0–0.6, the energy absorption performance of the structure is at the maximum level.

In this study, a simple and eco-friendly method was proposed to efficiently prepare nanocomposite hydrogels with excellent mechanical properties and satisfactory pH response behaviour by frontal polymerization of DEM in close to 4 minutes.

Deep eutectic solvent (DES) was prepared by using acrylic acid (AA) and acrylamide (AM) as hydrogen bonding donors (HBD) and choline chloride (ChCl) as hydrogen bonding receptors (HBA). Nitrogen-doped carbon nanotubes (N-CNTs) were dispersed in DES as fillers, and N-CNTs/P(AA-co-AM) composite hydrogels were prepared by FP. The interaction mode between the hydrogel and N-CNTs was characterized by Fourier infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The mechanical properties, pH response and electrical conductivity of the composite hydrogels were studied. The results showed that the mechanical properties of the hydrogel were significantly enhanced with the increase of N-CNT content. The tensile strength and compressive strength of the FP4 composite hydrogel reached 5.42 MPa and 4.29 MPa, respectively. Due to the dissociation of carboxyl groups in AA in an alkaline environment the composite hydrogel showed excellent pH response performance. The conductivity of the hydrogel was also found to be improved with the content of N-CNTs. When the content of N-CNTs is 1.0 wt%, the conductivity of the hydrogel was 4.2 times higher than that of the hydrogel without N-CNTs, and connecting it to a circuit can make an LED lamp emit bright light. In this study, a simple and green method was proposed to prepare composite hydrogels with excellent mechanical properties and electrical conductivity by FP of DES in less than 5 min.