The need for more effective defence systems is of critical importance because of the rising risk of explosive attacks. Sandwich panels are used as plastically deforming sacrificial structures, absorbing blast wave energy. To the authors’ knowledge, the blast behaviour of sandwich panels with connected (welded/bolted/riveted) corrugated layers has been well covered in literature. Hence, the aim of this numerical study was to develop new, easy-to-build, non-expensive, graded sandwich panel with ‘unconnected’ corrugated layers that can be used as a multipurpose sacrificial protective structure against wide range of blast threats. The proposed sandwich panel is composed of six unconnected aluminium (AL6063-T4) core layers encased in a steel (Weldox $460$E) frame with 330 × 330 × 150 mm overall dimensions. The numerical analysis was conducted using Abaqus/Explicit solver. First, the performance of four different nongraded layer topologies (trapezoidal, triangular, sinusoidal, and rectangular) was compared, when subjected to ~16 MPa peak reflected over-pressure (M = 0.5 kg of TNT at R = 0.5 m). Results showed that the trapezoidal topology outperformed other topologies, with uniform progressive collapse, lower reaction force, and higher plastic dissipation energy. Then, the trapezoidal topology was further analysed to design a ‘graded’ sandwich panel that can absorb a wide range of blast intensities (~4, 7, 11, 13, and 16 MPa peak reflected over-pressures) by using a (0.4, 0.8, 1.2 mm) stepwise thickness combination for the layers. In conclusion, the superior performance of the proposed sandwich panel with unconnected graded layers can be considered as a novel alternative to the conventional costly laser-welded sandwich panels. Applications of the new solution range from protecting civil structures to military facilities.

The paper presents theoretical, experimental and numerical studies on the thermal behavior of mineral wool used in sandwich panels. The aim of this study is to investigate the thermal properties of mineral wool at elevated temperatures and provide a simple model that would allow us to determine the heat propagation in sandwich panels during a fire. The paper proposes a new method to experimentally evaluate thermal diffusivity, derived from theoretical premises. Experiments are conducted in a laboratory furnace where specimens are placed and temperatures inside specimens are measured. Different methods are used to process the test results and calculate the thermal diffusivity of mineral wool. Finally, a numerical analysis of heat transfer using the finite element method (FEM) is performed to validate the obtained thermal properties.

In this paper, an experimental investigation is presented for sandwich panels with various core layer materials (polyisocyanurate foam, mineral wool, and expanded polystyrene) when subjected to a justified blast load. The field tests simulated the case for when 5 kg of trinitrotoluene (TNT) is localized outside a building’s facade with a 5150 mm stand-off distance. The size and distance of the blast load from the obstacle can be understood as the case of both accidental action and a real terroristic threat. The sandwich panels have a nominal thickness, with the core layer equal 100 mm and total exterior dimensions of 1180 mm × 3430 mm. Each sandwich panel was connected with two steel columns made of I140 PE section using three self-drilling fasteners per panel width, which is a standard number of fasteners suggested by the producers. The steel columns were attached to massive reinforced concrete blocks via wedge anchors. The conducted tests revealed that the weakest links of a single sandwich panel, subjected to a blast load, were both the fasteners and the strength of the core. Due to the shear failure of the fasteners, the integrity between the sandwich panel and the main structure is not provided. A comparison between the failure mechanisms for continuous (polyisocyanurate foam and expanded polystyrene) and non-continuous (mineral wool) core layer materials were conducted.

The paper presents theoretical, experimental and numerical studies on the thermal behavior of mineral wool used in sandwich panels. The aim of this study is to investigate the thermal properties of mineral wool at elevated temperatures and provide a simple model that would allow to determine the heat propagation in sandwich panels during fire. The paper proposes a new method to experimentally evaluate thermal diffusivity, derived from theoretical premises. Experiments are conducted in a laboratory furnace, where specimens are placed and temperatures inside specimens are measured. Different methods are used to process the test results and calculate the thermal diffusivity of mineral wool. Finally, a numerical analysis of heat transfer using finite element method (FEM) is performed to validate the obtained thermal properties.