Poly(ε-caprolactone) (PCL) is a hydrophobic, resorbable aliphatic polymer recognized for its low tenacity and extensive elongation at break, making it a popular choice for fabricating biodegradable tissue engineering scaffolds. PCL’s slow degradation rate typically results in a complete resorption period of 2 to 3 years. While numerous studies have examined the degradation of PCL in various forms such as films and webs, no study to date has investigated its physiological degradation in multifilament yarn form. In this study, we subjected PCL multifilament yarn samples to physiological conditions in phosphate-buffered saline (PBS) maintained at a consistent temperature of 37 ± 2 °C and agitated at 45 rpm for a period of 32 weeks. We retrieved samples at five different intervals to analyze the degradation profile of the multifilament yarn. This allowed us to estimate the complete resorption time and rate under these in vitro conditions. Over the 32-week period, the multifilament yarn’s mass decreased by 4.8%, its elongation at break declined by 42%, the tenacity dropped by 40%, and the peak load at break fell by 46.5%. Based on these findings, we predict that a scaffold structure incorporating PCL multifilament yarn would undergo complete resorption in approximately 14 months under physiological conditions, such as in PBS solution at a pH of approximately 7 and a temperature of 37 °C.

Craniofacial microsomia is a congenital deformity caused by asymmetric development of the skull (cranium) and face before birth. Current treatments include corrective surgery and replacement of the deformed structure using autograft tissue, which results in donor site morbidity. An alternative therapy can be achieved by developing a resorbable scaffold for skeletal muscle regeneration which will help restore the symmetry and function of the facial muscles and reduce donor site morbidity. Two resorbable weft knitted scaffolds were fabricated using poly(ε-caprolactone) multifilament yarns with unique auxetic design structures possessing negative Poisson’s ratio (NPR). These scaffolds exhibit their NPR elasticity through an increase in total volume as well as no lateral narrowing when stretched longitudinally, which can provide orientated mechanical supports to the cell growth of skeletal muscle regeneration. These scaffolds were evaluated for the required physical properties, mechanical performance and biocompatibility by culturing them with neonatal human dermal fibroblasts so as to determine their cell metabolic activity, cell attachment and proliferation. This study can facilitate the understanding and engineering of textile-based scaffolds for tissues/organs. The work also paves a pathway to emerge the NPR textiles into tissue engineering, which has an extensive potential for biomedical end-uses.

The use of tissue engineering to regenerate viable tissue relies on selecting the appropriate cell line, developing a resorbable scaffold and optimizing the culture conditions including the use of biomolecular cues and sometimes mechanical stimulation. This review of the literature focuses on the required scaffold properties, including the polymer material, the structural design, the total porosity, pore size distribution, mechanical performance, physical integrity in multiphase structures as well as surface morphology, rate of resorption and biocompatibility. The chapter will explain the unique advantages of using textile technologies for tissue engineering scaffold fabrication, and will delineate the differences in design, fabrication and performance of woven, warp and weft knitted, braided, nonwoven and electrospun scaffolds. In addition, it will explain how different types of tissues can be regenerated by each textile technology for a particular clinical application. The use of different synthetic and natural resorbable polymer fibers will be discussed, as well as the need for specialized finishing techniques such as heat setting, cross linking, coating and impregnation, depending on the tissue engineering application.