Electrochemical immunosensors have shown great potential in clinical diagnosis, food safety, environmental protection, and other fields. The feasible and innovative combination of enzyme catalysis and other signal-amplified elements has yielded exciting progress in the development of electrochemical immunosensors. Alkaline phosphatase (ALP) is one of the most popularly used enzyme reporters in bioassays. It has been widely utilized to design electrochemical immunosensors owing to its significant advantages (e.g., high catalytic activity, high turnover number, and excellent substrate specificity). In this work, we summarized the achievements of electrochemical immunosensors with ALP as the signal reporter. We mainly focused on detection principles and signal amplification strategies and briefly discussed the challenges regarding how to further improve the performance of ALP-based immunoassays.

To investigate the alternatives to lithium-ion batteries, potassium-ion batteries have attracted considerable interest due to the cost-efficiency of potassium resources and the relatively lower standard redox potential of K⁺/K. Among various alternative anode materials, hard carbon has the advantages of extensive resources, low cost, and environmental protection. In the present study, we synthesize a nitrogen-doping hard-carbon-microsphere (N-SHC) material as an anode for potassium-ion batteries. N-SHC delivers a high reversible capacity of 248 mAh g⁻¹ and a promoted rate performance (93 mAh g⁻¹ at 2 A g⁻¹). Additionally, the nitrogen-doping N-SHC material also exhibits superior cycling long-term stability, where the N-SHC electrode maintains a high reversible capacity at 200 mAh g⁻¹ with a capacity retention of 81% after 600 cycles. DFT calculations assess the change in K ions’ absorption energy and diffusion barriers at different N-doping effects. Compared with an original hard-carbon material, pyridinic-N and pyrrolic-N defects introduced by N-doping display a positive effect on both K ions’ absorption and diffusion.

In recent years, atomic-doping has been proven to significantly improve the electrochemical performance of biomass-derived carbon materials, which is a promising modification strategy. Among them, there are relatively few reports about O-doping. Here, porous carbon derived from orange peel was prepared by simple carbonization and airflow-annealing processes. Under the coordination of microstructure and surface groups, the derived carbon had excellent electrochemical performance for the K-ion batteries’ anode, including a high reversible specific capacity of 320.8 mAh/g, high rate performance of 134.6 mAh/g at a current density of 2000 mA/g, and a retention rate of 79.5% even after 2000 long-term cycles, which shows great application potential. The K-ion storage mechanisms in different voltage ranges were discussed by using various characterization techniques, that is, the surface adsorbed of K-ionswas in the high-potential slope area, and the intercalation behavior corresponded to the low-potential quasi-plateau area. In addition, the density functional theory calculations further confirmed that O-doping can reduce the adsorption energy barrier of K-ions, change the charge density distribution, and promote the K-ion storage. In particular, the surface Faraday reaction between the C=O group and K-ions plays an important role in improving the electrochemical properties.

The development of efficient and stable catalysts with high mass activity is crucial for acidic oxygen evolution reaction (OER). In this study, CeO₂-Ir heterojunctions supported on carbon nanotubes (CeO₂-Ir/CNTs) are synthesized using a solvothermal method based on the heterostructure strategy. CeO₂-Ir/CNTs demonstrate remarkable effectiveness as catalysts for acidic OER, achieving 10.0 mA cm⁻² at a low overpotential of only 262.9 mV and maintaining stability over 60.0 h. Notably, despite using an Ir dosage 15.3 times lower than that of c-IrO₂, CeO₂-Ir/CNTs exhibit a very high mass activity (2542.3 A g_Ir⁻¹@1.53 V), which is 58.8 times higher than that of c-IrO₂. When applied to acidic water electrolyzes, CeO₂-Ir/CNTs display a prosperous potential for application as anodic catalysts. X-ray photoelectron spectrometer (XPS) analysis reveals that the chemical environment of Ir nanoparticles (NP) can be effectively modulated through coupling with CeO₂. This modulation is believed to be the key factor contributing to the excellent OER catalytic activity and stability observed in CeO₂-Ir/CNTs.