Chitosan and its derivatives are widely used in food packaging, pharmaceutical, biotechnology, medical, textile, paper, agriculture, and environmental industries. However, the flexibility of chitosan films is extremely poor, which limits its relevant applications to a large extent. In this paper, chitosan/sorbitol/nano-silica (CS/sorbitol/SiO₂) composite films were prepared by the casting film method using chitosan, sorbitol, Tween-80 and nano-SiO₂ as raw materials. The structure of the films was characterized by infrared spectroscopy, electron scanning microscopy, and X-ray diffraction analysis. The effects of sorbitol and nano-silica dosage on the mechanical properties, thermal properties and water vapor barrier properties of the composite film were investigated. The results show that with the gradual increase in sorbitol (≤75 wt %), the elongation at the break of chitosan/sorbitol films significantly increased. When the addition of sorbitol was 75 wt %, the elongation at break of the chitosan/sorbitol composite film was 13 times higher than that of the chitosan film. Moreover, nano-SiO₂ can further improve the mechanical properties and thermal stability of the chitosan/sorbitol composite films. When the amount of nano-silica was 4.5 wt %, the composite film became more flexible, with a maximum elongation of 90.8% (which is 14 times that of chitosan film), and its toughness increased to 10.52 MJm⁻³ (which is 6 times that of chitosan film). This study balances the tensile strength and elongation at break of the composite films by adding a plasticizer and nano-filler, providing a reference for the preparation of chitosan composites or their blending with other polymers, and has practical guiding significance for the industrial production of biomass plastics.

Biological hydrogels are widely available in terms of raw material sources and can be processed and molded using relatively simple techniques. Hydrogels can offer abundant three-dimensional, water-containing channels that facilitate the reaction between gases and dye, making them the preferred choice for the solid support layer in colorimetric indicators. However, biomass hydrogels exhibit inferior mechanical properties, making them unsuitable for large-scale manufacturing processes. In this study, four dual-network composite hydrogels Agar/Gelatin, Sodium Alginate/Agar, Sodium Alginate/Poly (vinyl alcohol), Sodium Alginate/Gelatin (AG/Gel, SA/AG, SA/PVA and SA/Gel) prepared through hybrid strategies. Furthermore, the influence of the dual-network structure on the mechanical properties and ammonia response was systematically investigated, using microscopy and Fourier transform infrared spectroscopy (FTIR) characterization method. The experimental results demonstrate that the incorporation of SA into original hydrogel matrices can significantly enhance both the mechanical and ammonia response performance due to the secondary topological network structure. The interpenetrating double network structure was effectively regulated through the calcium ion cross-linking process. The color difference threshold of SA/PVA’s response to ammonia gas is 10, it holds promise for rapid detection applications. The SA/Gel composite hydrogel exhibits excellent mechanical robustness and toughness. The tensile strength of the SA/Gel sample is 11 times that of a single gel, and the toughness is 80 times greater, suggesting its suitability for large-scale manufacturing of colorimetric indicator.