Ultralow wear rates and low friction have been observed for carbon fiber reinforced PTFE (CF/PTFE) when sliding against steel or cast iron in dry gas environments. Although the strong environmental sensitivity of this tribosystem is well known, the origin of the outstanding tribological performance in dry gas remains unanswered. Some researchers attribute the low friction and wear to the formation of carbon-rich surfaces in the absence of oxygen and moisture in the environment. However, low friction between carbon surfaces is generally dependent on moisture. In this paper, extensive analyzes are conducted on the tribofilms formed on the CF/PTFE surface and the steel counterface after sliding in a high-purity nitrogen environment. TEM analysis of a cross-section of the tribofilm on the steel surface reveals that the sliding surface consists mainly of iron (II) fluoride and not carbon, even though a significant amount of carbon was observed near the surface. XPS and TEM analysis further revealed that the tribofilm formed on the worn composite surface consisted of nanoparticle agglomerates, anchored to the PTFE matrix and to each other by carbon with turbostratic structure. Turbostratic carbon also formed an ultrathin and surface-oriented superficial layer on top of the agglomerates. Governing mechanisms of the low friction and wear of the CF/PTFE—steel tribosystem were investigated by complementary tribotests with pure graphite samples and MD simulations of the identified surfaces. These indicated that the low friction between the carbon and iron fluoride in the tribofilms is due to poor adhesion between the distinctly different surfaces. Graphical Abstract

Carbon fiber reinforced polytetrafluoroethylene (CF/PTFE) composites are known for their exceptional tribological performance when sliding against steel or cast iron in inert gas environments. Compared to experiments in humid air, about an order of magnitude lower wear rate and several times lower coefficient of friction have been reported for tests conducted in dry nitrogen and hydrogen. Moreover, trace moisture has been shown to affect the friction and wear significantly of this tribosystem, although a possible effect of oxygen cannot be ruled out due to uncertainties regarding the oxygen concentrations. While several studies have pointed out the environmental sensitivity of CF/PTFE, the understanding of the underlying mechanisms are very limited. The objective of this research is to investigate the individual and combined effect of oxygen and moisture on the tribological behavior of CF/PTFE sliding against steel. Additionally, this study aims to elucidate the underlying mechanisms that govern the environmental sensitivity of the system. Climate-controlled three-pin-on-disc experiments were conducted in nitrogen atmospheres at various concentrations of oxygen and moisture. The tribological results clearly demonstrate that both moisture and oxygen contribute to increased friction and wear. However, the adverse effect was much more pronounced for oxygen than moisture. A qualitative method was developed to estimate the tribofilm coverage on the CF/PTFE surface. Results showed strong correlation between high coverage of strongly adhered tribofilm and low wear rate. Moreover, a loosely adhered tribofilm was observed on top of the CF/PTFE surface in presence of moisture. FTIR analysis indicated that the loosely adhered tribofilm found in the moisture-enriched environment contained a significant amount of adsorbed water, which may explain the lower coefficient of friction in presence of moisture compared to oxygen. The adsorbed water in the loosely adhered tribofilm could be an indication of moisture-driven lubrication by the non-graphitic carbon in the tribofilm.

Carbon fiber-reinforced polytetrafluoroethylene (CF/PTFE) composites are frequently used in tribological dry gas applications, such as in dynamic seals in reciprocating hydrogen gas compressors and Stirling engines, due to their superior friction and wear. Due to the increasing concerns regarding fluoropolymers as possible pollutants of harmful per- and poly-fluoroalkyl substances (PFAS) emissions, replacements for PTFE should be investigated. The literature indicates that CF-reinforced polyetheretherketone (CF/PEEK) may have similar favorable tribological properties to CF/PTFE. However, the tribological behavior of CF/PEEK in dry gas is poorly understood, and no direct comparison has been made between the two materials. The aim of this study was to compare the effect of oxygen and moisture on the friction and wear of CF/PTFE and CF/PEEK. Tribological tests were carried out with a tri-pin-on-disc tribometer in a nitrogen environment with individually controlled contents of oxygen and moisture. The results showed that the effect of oxygen and moisture are distinctly different for CF/PTFE and CF/PEEK. While CF/PTFE performs best in oxygen-deficient environments, CF/PEEK performs best in moisture-enriched environments. Complementary tests with a PTFE composite filled with both CF and PEEK suggested that the environmental sensitivity can be significantly reduced by combining the two polymers.

Research in tribology are often connected to tribosystems operating in specific environments, where climate chambers are needed for tribotesting to resemble the environmental conditions in the real application. Although the effect of humidity on the tribological performance of many materials and lubricants is evident, many studies are conducted without sufficient systems to accurately monitor and control the humidity level throughout testing. In this paper, a humidity controlling system was developed to enable continuous monitoring and precise control of the humidity at trace moisture levels. The climate controller was validated in a tri-pin-on-disc tribometer with excellent performance and can be fitted to most climate chambers. To further improve the control of operating conditions during tribotesting, a thermodynamic simulation of the contact temperature was developed. • The developed climate controller is a simple and cost-effective method to accurately monitor and control the humidity in a climate chamber at trace moisture levels. • The portable design of the humidity controller enables use with most climate chambers and enclosed tribometers. • To have better control over the temperature in the sliding interface during testing, a thermodynamic simulation method was used to estimate contact temperature between sliding bodies from near-contact temperature measurements and the measured friction forces.