In the context of sustainable solutions, this study examines the pyrolysis process applied to corn cobs, with the aim of producing biochar and assessing its effectiveness in combating air pollution. In particular, it examines the influence of different pyrolysis temperatures on biochar properties. The results reveal a temperature-dependent trend in biochar yield, which peaks at 400 °C, accompanied by changes in elemental composition indicating increased stability and extended shelf life. In addition, high pyrolysis temperatures, above 400 °C, produce biochars with enlarged surfaces and improved pore structures. Notably, the highest pyrolysis temperature explored in this study is 600 °C, which significantly influences the observed properties of biochars. This study also explores the potential of biochar as an NO₂ adsorbent, as identified by chemical interactions revealed by X-ray photoelectron spectroscopy (XPS) analysis. This research presents a promising and sustainable approach to tackling air pollution using corn cob biochar, providing insight into optimized production methods and its potential application as an effective NO₂ adsorbent to improve air quality.

The development of antimicrobial devices and surfaces requires the setup of suitable materials, able to store and release active principles. In this context, zeolites, which are microporous aluminosilicate minerals, hold great promise, since they are able to serve as a reservoir for metal-ions with antimicrobial properties. Here, we report on the preparation of Linde Type A zeolites, partially exchanged with combinations of metal-ions (Ag⁺, Cu²⁺, Zn²⁺) at different loadings (0.1–11.9 wt.%). We combine X-ray fluorescence, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction to monitor the metal-ion contents, distribution, and conservation of the zeolite structure after exchange. Then, we evaluate their antimicrobial activity, using agar dilution and optical-density monitoring of Escherichia coli cultures. The results indicate that silver-loaded materials are at least 70-fold more active than the copper-, zinc-, and non-exchanged ones. Moreover, zeolites loaded with lower Ag⁺ concentrations remain active down to 0.1 wt.%, and their activities are directly proportional to the total Ag content. Sequential exchanges with two metal ions (Ag⁺ and either Cu²⁺, Zn²⁺) display synergetic or antagonist effects, depending on the quantity of the second metal. Altogether, this work shows that, by combining analytical and quantitative methods, it is possible to fine-tune the composition of bi-metal-exchanged zeolites, in order to maximise their antimicrobial potential, opening new ways for the development of next-generation composite zeolite-containing antimicrobial materials, with potential applications for the design of dental or bone implants, as well as biomedical devices and pharmaceutical products.

In this study, a layer of a pure and dense phase of FAU-type zeolite was synthesized directly on the surface of α-Al₂O₃ plane macroporous support. Before hydrothermal synthesis, a step of cleaning of the support by an anionic detergent was performed, a roughness surface is created, allowing the anchoring of the zeolite nuclei and then their growth, favoring in this sense the formation of a homogeneous zeolite layer. The obtained membranes were fully characterized using X-ray diffraction analysis (XRD), nitrogen sorption, scanning electron microscopy (SEM), and mercury porosimetry. After 24 h of thermal treatment at 75 °C, a homogeneous zeolite layer composed of bipyramidal crystals of FAU-type zeolite is obtained with a thickness of about 2.5 µm. No obvious defects or cracks can be observed. It was found that the increase in heating temperature could lead to the appearance of an impurity phase, GIS-type zeolite. Then the ideal zeolite membrane was exchanged with Ag⁺ or Zn²⁺ cations to studies their antimicrobial properties. Zeolites membranes exchanged with Ag⁺ showed an agar-diffusive bactericidal activity against gram negative Escherichia coli (E. coli) bacteria. Zn²⁺ exchanged zeolite membrane presented a bacteriostatic activity that is less diffusive in agar. As expected, non-exchanged zeolite membrane (in its Na⁺ form) have no effect on bacterial activity. This process is particularly interesting for the synthesis of a good quality FAU-type zeolite membranes with antimicrobial properties.

Reported here are new data on the structural and catalytic properties of a series of mono-component cobalt and bi-component Co–Ce catalysts supported on SBA-15 (Santa Barbara Amorphous-15)). The catalysts performance has been evaluated by tests on combustion of methane, propane, and n-hexane. It was established that the preparation of the Co–Ce catalysts by the ‘two-solvent’ technique does not significantly change the mesoporous structure, however, its pores are clogging with the Co and Ce guest species. Cobalt and cerium are uniformly distributed and preferentially fill up the channels of SBA-15, but oxide agglomerates located on the surface are observed as well. The highest activity of the mono-component cobalt sample is explained by its higher reducibility as a result of lower interaction of the cobalt oxide with the SBA-15. The fine dispersion of cobalt and cerium oxide and their strong interaction in the channels of the SBA-15 molecular sieve, leads to the formation of difficult-to-reduce oxide phases and, consequently, to lower catalytic activity compared to monocomponent cobalt oxide catalyst. The synthesised mesoporous structure can prevent the agglomeration of the oxide particles, thus leading to the successful development of a new and stable catalyst for decreasing greenhouse gas emissions.

Calcium oxalate phytoliths are one of the most prominent types of Ca speciation in the plant kingdom, and they store extensive amounts of carbon in crystalline form. Ca phytoliths were investigated in the root, trunk, and bark of Vitis vinifera Chasselas from a vineyard in Alsace, France. A multi-analytical approach was used, which included SEM coupled with EDX spectroscopy, XRD, XRF, TGA, and ¹³C-NMR spectroscopy. These techniques revealed that phytoliths are composed of crystalline calcium oxalate monohydrate (whewellite). The whewellite crystals exhibited mostly equant or short-prismatic habits in all of the three studied grapevine parts, but bipyramidal crystals also occurred. Raphide crystals were only observed in the root, where they were abundant. Instead of using wet chemical procedures to extract the mineral components from the organic parts of the biomass, a thermal treatment via calcination was chosen. The suitable temperature of calcination was determined through TGA experiments. The calcination of the biomass samples at 250 °C enhanced the amounts of Ca phytoliths in the residual chars. The thermal treatment, however, affected the appearance of the Ca oxalate crystals by producing surfaces that displayed macroporosity and by creating fractures. For calcination at both 300 °C and 350 °C, Ca oxalate lost a molecule of carbon monoxide to form Ca carbonate, and the modifications of the original crystal surfaces were more pronounced than those observed after thermal treatment at 250 °C.

In contrast with the conventional CoMoS/alumina catalyst, the use of amorphous mesostructured ZrO₂ as support for the dispersion of the CoMoS active phase in deep hydrodesulfurization (HDS) of 4,6-dimethyldibenzothiophene led to a higher promotion rate and a better sulfidation of the cobalt species. The CoMoS, dispersed over mesostructured amorphous ZrO₂ as catalyst, also induced a modification of the main desulfurization way; in this case, a shift towards direct desulfurization selectivity was observed. This result was unexpected regarding the literature. Indeed, the hydrogenated route was observed for commercial zirconia. The designed catalysts are therefore more eco-friendly, since they consume less hydrogen. This implies a better use of the fossil resources.