In order to find new ways to ensure sustainable development on a global level, it is essential to combine current top technologies, such as additive manufacturing, with the economic, ecological, and social fields. One objective of this paper refers to wire manufacture such as Arboblend V2 Nature, Arbofill Fichte, and Arboblend V2 Nature reinforced with Extrudr BDP “Pearl” (BDP—Biodegradable Plastic) in order to replace the plastic materials. After wire manufacture by extrusion, the diameter accuracy was analyzed compared with the Fiber Wood wire using SEM analyses and also EDAX—Energy Dispersive X-ray Analysis and DSC—Differential Scanning Calorimetry analyses were done in order to identify their elemental composition and the phase transitions suffered by the materials during heating. Using the samples obtained through the Fused Deposition Modeling (FDM) method, both crystalline phases and chemical composition information (XRD analysis) were identified, as well was determined the visco-elastic behavior Dynamic Mechanical Analysis (DMA), for the reinforced material and Fiber Wood. The extruded wires have allowed size for the printing equipment, around 1.75 mm with tolerance of ± 0.05 mm. The wire material diagrams, Arboblend V2 Nature reinforced with Extrudr BDP “Pearl” and Fiber Wood following the calorimetric analysis, presented peaks corresponding to material crystallization, while Arbofill Fichte revealed only the melting temperature. The storage module was almost double in case of Arboblend V2 Nature reinforced with Extrudr BDP “Pearl” compared with Fiber Wood and materials’ melting temperatures were confirmed by the analyses carried out.

It is essential to combine current state-of-the-art technologies such as additive manufacturing with current ecological needs. Due to the increasing demand for non-toxic biodegradable materials and products, human society has been searching for new materials. Consequently, it is compulsory to identify the qualities of these materials and their behavior when subjected to various external factors, to find their optimal solutions for application in various fields. This paper refers to the biodegradable Polylactic acid (PLA)-based filament (commercially known as Extrudr BDP (Biodegradable Plastic) Flax) compared with the biodegradable composite material PLA-lignin filament whose constituent’s trade name is Arboblend V2 Nature as a lignin base material and reinforcement with Extrudr BDP Pearl, a PLA based polymer, 3D printed by Fused Deposition Modeling technology. Certain mechanical properties (tensile strength, bending strength and DMA—Dynamic Mechanical Analysis) were also determined. The tribology behavior (friction coefficient and wear), the structure and the chemical composition of the biodegradable materials were investigated by SEM—Scanning Electron Microscopy, EDX—Energy Dispersive X-Ray Analysis, XRD—X-Ray Diffraction Analysis, FTIR—Fourier Transform Infrared Spectrometer and TGA—Thermogravimetric Analysis. The paper also refers to the influence of technological parameters on the 3D printed filaments made of Extrudr BDP Flax and the optimization those of technological parameters. The thermal behavior during the heating of the sample was analyzed by Differential scanning calorimetry (DSC). As a result of the carried-out research, we intend to recommend these biodegradable materials as possible substituents for plastics in as many fields of activity as possible.

Biodegradable materials investigation has become a necessity and a direction for many researchers worldwide. The main goal is to find sustainable alternatives which gradually replace plastics based on fossil resources from the market, because they are very harmful to the environment and to overall quality of life. In order to get to the stage of obtaining different functional parts from biodegradable materials, it is necessary to study their properties. Taking into account these shortcomings, this paper aims at the mechanical characterization (DMA—Dynamic Mechanical Analysis) and thermal degradation (thermogravimetric analysis (TGA)) of lignin-based biopolymers: Arboform LV3 Nature^®, Arboblend^® V2 Nature, and Arbofill^® Fichte Arboform^® LV3 Nature reinforced with aramid fibers. The tested samples were obtained by using the most common fabrication technique for polymers—injection molding. The obtained results for the DMA analysis showed separate polymeric-specific regions for each material and, based on the tanδ values between (0.37–0.54), a series of plastics could be proposed for replacement. The mechano-dynamic behavior could be correlated with the thermal expansion of biopolymers for temperatures higher than 50/55 °C, which are thermally stable up to temperatures of at least 250 °C.

This work presents an experimental analysis related to 3D-printed carbon-fiber-reinforced-polymer (CFRP) machining. A polyethylene-terephthalate-glycol (PETG)-based composite, reinforced with 20% carbon fibers, was selected as the test material. The aim of the study was to evaluate the influence of cutting conditions used in light operations on the generated surface quality of the 3D-printed specimens. For this purpose, nine specimens were fabricated and machined under a wide range of cutting parameters, including cutting speed, feed, and depth of cut. The generated surface roughness was measured with a mechanical gauge and the acquired data were used to develop a shallow artificial neural network (ANN) for prediction purposes, showing that a 3-6-1 structure is the best solution. Following this, a genetic algorithm (GA) was utilized to minimize the response, revealing that the optimal combination is 205 m/min speed, 0.0578 mm/rev feed, and 0.523 mm depth of cut, contributing to the fabrication of low friction parts and shafts with a high quality surface, as well as to the reduction of resource waste. A validation study supported the accuracy of the developed model, by exhibiting errors below 10%. Finally, a set of enhanced images were taken to assess the machined surfaces. It was found that 1.50 mm depth of cut is responsible for the generation of defects across the circumference of the specimens. Especially, combined with 150 m/min cutting speed and 0.11 mm/rev feed, more flaws are produced.

Recent developments in incremental sheet forming have resulted in the creation of novel manufacturing processes that are highly adaptable and could bring significant economic benefits for advanced technologies and low-volume production. In this manuscript, the following variables were examined: the variation in the deformation forces for a part with a pyramidal trunk shape; the variation in the deformations and thinning of the Al 3003 material during the incremental forming process; and the variation in the accuracy of the incrementally formed part and the quality of the surfaces (surface roughness). The components of the forces in the incremental forming have increasing values from the beginning of the process to the maximum value due to the hardening process. The TiN-coated tool ensures lower values of the forming components. Due to the kinematics of the forming process, deviations, especially in shape, from the part in the drawing are observed, which are shown by the radius of curvature of the side wall of the part, the appearance of a radius of connection between the wall and the bottom of the part, as well as dimensional deviations that are expressed by the variation in the forming depth. Concerning the smoothness of the surfaces, it was observed that the best roughness results were obtained in the case of the TiN-coated tool.

The paper aims to investigate the behavior of Arboblend V2 Nature biopolymer samples covered with three ceramic powders, Amdry 6420 (Cr₂O₃), Metco 143 (ZrO₂ 18TiO₂ 10Y₂O₃) and Metco 136F (Cr₂O₃-xSiO₂-yTiO₂). The coated samples were obtained by injection molding, and the micropowder deposition was achieved by using the Atmospheric Plasma Spray (APS) method, with varied thickness layers. The present study will only describe the results for nine-layer deposition because, as the number of layers’ increases, the surface quality and mechanical/thermal characteristics such as wear, hardness and thermal resistance are also increased. The followed determinations were conducted: the adhesion strength, hardness on a microscopic scale by micro-indentation, thermal analysis and structural and morphological analysis. The structural analysis has highlighted a uniform deposition for the ZrO₂ 18TiO₂ 10Y₂O₃ layer, but for the layers that contained Cr₂O₃ ceramic microparticles, the deposition was not completely uniform. The thermal analysis revealed structural stability up to a temperature of 230 °C, the major degradation of the biopolymer matrix taking place at a temperature around 344 °C. The samples’ crystalline structure as well as the presence of the Cr₂O₃ compound significantly influenced the micro-indentation and scratch analysis responses. The novelty of this study is given by itself the coating of the Arboblend V2 Nature biopolymer (as base material), with ceramic microparticles as the micropowder coating material. Following the undertaken study, the increase in the mechanical, tribological and thermal characteristics of the samples recommend all three coated biopolymer samples as suitable for operating in harsh conditions, such as the automotive industry, in order to replace plastic materials.