Under slightly acidic conditions and 25 °C, the interaction between phosphate-rich aqueous solutions and gypsum cleavage fragments results in the surface precipitation of brushite (CaHPO₄·2H₂O) crystals, which grow epitaxially on the (010) surface of gypsum. Using an A-centered unit-cell setting for both brushite (Aa) and gypsum (A2/a), the epitaxial relationship implies matching of the planes (010) of both structures and correspondence between equivalent crystallographic directions within these planes. The crystal habit of the overgrowing brushite is thin tabular to laminar on {010} with {111̅} and {111} as side faces and a clear elongation on [101]. There are two orientations of the brushite plates on the gypsum surface related to each other by a twofold axis on [010]. Thus, the overgrowth is an aggregate of parallel brushite crystals that may be twin-related, with the twofold axis as the twin law. During the interaction, gypsum dissolution is coupled with brushite growth until saturation with respect to both minerals is reached. A model of this thermodynamically driven dissolution-crystallization process is presented using the geochemical code PHREEQC. The epitaxial relationships are explained by comparing the bond system and the crystallographic properties of both minerals.

The epitaxial overgrowth of brushite (CaHPO₄·2H₂O) by the interaction of phosphate-bearing, slightly acidic, aqueous solutions with gypsum (CaSO₄·2H₂O) was investigated in situ using atomic force microscopy (AFM). Brushite growth nuclei were not observed to form on the {010} gypsum cleavage surface, but instead formed in areas of high dissolution, laterally attached to gypsum [101] step edges. During the brushite overgrowth the structural relationships between brushite (Aa) and gypsum (A2/a) result in several phenomena, including the development of induced twofold twining, habit polarity, and topographic effects due to coalescence of like-oriented crystals. The observed brushite growth is markedly anisotropic, with the growth rate along the main periodic bond chains (PBCs) in the brushite structure increasing in the order [101] > [1̅01] > [010], leading to tabular forms elongated on [101]. Such a growth habit may result from the stabilization of the polar [101] direction of brushite due to changes in hydration of calcium ions induced by the presence of sulfate in solution, which is consistent with the stabilization of the gypsum [101] steps during dissolution in the presence of HPO₄²⁻ ions. The coupling between growth and dissolution was found to result in growth rate fluctuations controlled by the changes in the solution composition.