This study was to investigate the morphology, structure, and chemical properties of the Mendong fibers extracted from Mendong grass (Fimbristylis globulosa) in the form of raw and treated fiber by alkali-included chemical content and functional group and to evaluate the strength and properties of Mendong fibers compared with other natural fibers. These studies explore the chemical properties of the fiber including fiber composition and functional group by FTIR, mechanical properties of fiber, and the structural and morphological analysis of the fiber using SEM and XRD. The results showed that the chemical contents of Mendong fibers were 72.14% cellulose, 20.2% hemicellulose, 3.44% lignin, 4.2% extractive, and moisture of 4.2%–5.2%. Mechanical properties of the fiber were a strong character with tensile strength of 452 MPa, and modulus of 17 GPa. The structural properties of Mendong fiber such as crystallinity, crystalline index, microfibril angle, and crystalline size were 70.17% and 58.6%, 22.9°, and 14.3 nm, respectively. This fiber has competitive advantages compared with other natural fibers and can be developed further as a potential reinforcement of polymer matrix composites.

The research aim is to investigate the effect of alkali treatment on the crystalline structure of Mendong fiber. The experiment was conducted by immerse fibers in 100 ml NaOH solution by a concentration of 2.5%, 5%, 7.5%, and 10% for 2 hours at the room temperature. The specimens were characterized by X-ray diffraction method. The morphology of fiber treated by alkali was observed by Scanning Electron Microscope. The result shows that the crystalline structure of cellulose in Mendong fiber was changed in alkali treatment. It was found that both the degree of crystallinity and crystalline index of Mendong fiber was increased until alkali treatment concentration of 7.5%.

In the present work, the properties of cellulose extracted from mendong fiber have been investigated. The experiments were conducted by two different methods to extract the cellulose from mendong fiber, which is extracted by alkali and alkali assisted by PEF. The cellulose was analyzed using X-ray diffraction, Fourier Transform Infra Red, Thermogravimetric Analysis, and compared with cellulose of commercial product. The morphology of cellulose after extraction was observed using both optical and Scanning Electron Microscope. The crystalline structure properties of cellulose extracted from mendong fiber assisted by pulsed electric field (PEF) were similar to the commercial cellulose.