The synthesis of new composite nanomaterials based on graphene oxide (GO)modified with cellulose and its derivatives, as well as nanocellulose, is currently an important direction and contributes toward solving many problems in various fields such as nanotechnology, information technology, medicine, high-dielectric materials, and nanoelectronics. In this work, for the first time, for the production of GO and its membrane with carboxymethylcellulose (CMC), local Kazakhstan “Ognevsky” graphite was used as the initial raw material. In this regard, the preparation of nanocomposites of GO modified with cellulose derivatives, including CMC, attracts great interest from scientists and expands its field of practical application due to the significant changes in its physicochemical properties. In this work, the GO obtained using the Hummers method was modified by CMC, and its physicochemical, structural, and electrical characteristics were studied. The GO/CMC membrane was synthesized by mixing 1% GO with crushed solid mass of CMC (0.03 g; 0.06 g; 0.15 g) and then processing using ultrasound. The surface morphology of the GO/CMC membrane was studied using scanning electron microscopy (SEM). It has been established that by increasing the mass of CMC (0.03 g; 0.06 g; 0.15 g), the polymerization of CMC occurs on the surface of GO nanosheets. Cross-sectional micrographs of GO/CMC show the formation of sandwich-like layered structures. The synthesis efficiency (yield) of GO from synthetic graphite is 10.8%, and GO from Ognevsky graphite is 11.9%, almost 1.1% more than GO from synthetic graphite. The mechanical tensile strength increases from 2.3 MPa to 14.3 MPa and the Young’s modulus from 2.3 MPa to 143 MPa. The electrical parameters of the humidity sensor based on GO and GO/CMC membranes (0.03 g; 0.06 g; 0.15 g) were studied as a function of humidity to determine the performance of the device.

In nowadays, the synthesis of new composite nanomaterials based on graphene oxide (GO) modified with cellulose and its derivatives, as well as nanocellulose, is an important direction and contributes to solve many problems in various fields such as: nanotechnology, information technology, medicine, high-dielectric materials and nanoelectronics. In this work, for the first time, for the production of GO and its membrane with carboxymethylcellulose (CMC), local Kazakhstan “Ognevsky” graphite was used as the initial raw material. In this regard, the preparation of nanocomposites of GO modified with cellulose derivatives, including CMC, attracts great interest from scientists and expands its field of practical application due to the amazing changes of physicochemical properties. In the work, the GO obtained by the Hummers method was modified by CMC, with following study of its physicochemical, structural and electrical characteristics. The GO/CMC membrane was synthesized by mixing 1% GO with crushed solid mass of CMC (0.03 g; 0.06 g; 0.15 g) and then was processed by ultrasound. The surface morphology of the GO/CMC membrane were studied using Scanning electron microscopy (SEM). It has been established that with an increasing in the mass of CMC (0.03 g; 0.06 g; 0.15 g), polymerization of CMC occurs on the surface of GO nanosheets. Cross-sectional micrographs of GO/CMC show the formation of sandwich-like layered structures.