New inorganic nanostructured matrices for fiber-reinforced composites with enhanced high-temperature stability were developed from alkali aluminosilicate polymers doped with different ultra-high-temperature ceramic (UHTC) particles. The alkali aluminosilicate matrices were synthesized at room temperature with a high SiO₂:Al₂O₃ ratio and then further functionalized by doping with 4–5 wt % of micrometric SiC, ZrB₂, ZrC, and HfC powders and finally thermally stabilized as glass–ceramics at 750 °C. The different UHTC-doped matrices were characterized according to their dimensional and microstructural changes after thermal cycling in air flux at 1000 °C. The first results showed that carbide-based UHTC powders improved the thermal stability of the matrices, preventing the excessive swelling of the material and the formation of detrimental voids that might result in the lack of adhesion with reinforcing fibers. Contrarily, the addition of ZrB₂ resulted in an excessive matrix swelling at high temperature, thus proving no efficacy compared to the undoped matrix. Impregnation tests carried out on C-fiber fabrics showed good processability, adhesion to the fibers, and fracture pull-out, especially for carbide-based matrices.

Synthetic microfibres released during textile drying are considered an emerging source of microplastic pollution, yet this waste stream is generally discarded without treatment. This study investigates a valorisation route by incorporating waste dryer-filter microfibres into a potassium-based/metakaolin geopolymeric coating for architectural applications, with the dual objective of preventing environmental release and enhancing material performance. Geopolymer pastes containing 0.1–0.3 wt.% of synthetic microfibres were characterised in terms of physical, mechanical and microstructural behaviour. Microfibre addition produced a marked toughening effect, with flexural strength increasing from about 3 MPa for the unreinforced matrix to 7.5 MPa for the composite containing 0.3 wt.% fibres, while compressive strength decreased moderately due to the presence of a compliant fibrous phase. Microstructural observations confirmed fibre dispersion and fibre–matrix bonding, supporting crack-bridging mechanisms. Density, porosity and water absorption measurements indicated a stable geopolymer gel structure with a connected pore network. Thin-layer applications onto clay brick exhibited satisfactory workability and adhesion, confirmed by pull-off testing (~0.12 MPa) and interfacial microscopy. The results demonstrate that textile-derived microfibres can be effectively immobilised within a potassium geopolymer matrix while improving flexural performance, offering a feasible circular strategy for microfibre waste reuse in mineral coatings.