Reduced graphene oxide (rGO) has been studied as a resistive ammonia gas sensor at room temperature. The sensitive hybrid material composed of rGO and nano-silver ink (Ag-ink) was loaded on a microstrip patch antenna to realize high-performance wireless ammonia sensors. The material was investigated using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Firstly, interdigital electrodes (IDEs) printed on the polyethylene terephthalate (PET) by direct printing were employed to measure the variation of resistance of the sensitive material with the ammonia concentration. The results indicated the response of sensor varied from 4.25% to 14.7% under 15–200 ppm ammonia concentrations. Furthermore, the hybrid material was loaded on a microstrip patch antenna fabricated by a conventional printed circuit board (PCB) process, and a 10 MHz frequency shift of the sensor antenna could be observed for 200 ppm ammonia gas. Finally, the wireless sensing property of the sensor antenna was successfully tested using the same emitted antenna outside the gas chamber with a high gain of 5.48 dBi, and an increased reflection magnitude of the emitted antenna due to the frequency mismatch of the sensor antenna was observed. Therefore, wireless ammonia gas sensors loaded on a patch antenna have significant application prospects in the field of Internet of Things (IoTs).

A high-efficiency photodetector consisting of colloidal PbS quantum dots (QDs) and single-layer graphene was prepared in this research. In the early stage, PbS QDs were synthesized and characterized, and the results showed that the product conformed with the characteristics of high-quality PbS QDs. Afterwards, the photodetector was derived through steps, including the photolithography and etching of indium tin oxide (ITO) electrodes and the graphene active region, as well as the spin coating and ligand substitution of the PbS QDs. After application testing, the photodetector, which was prepared in this research, exhibited outstanding properties. Under visible and near-infrared light, the highest responsivities were up to 202 A/W and 183 mA/W, respectively, and the highest detectivities were up to 2.24 × 10¹¹ Jones and 2.47 × 10⁸ Jones, respectively, with light densities of 0.56 mW/cm² and 1.22 W/cm², respectively. In addition to these results, the response of the device and the rise and fall times for the on/off illumination cycles showed its superior performance, and the fastest response times were approximately 0.03 s and 1.0 s for the rise and fall times, respectively. All the results illustrated that the photodetector based on PbS and graphene, which was prepared in this research, possesses the potential to be applied in reality.