Environmental concerns regarding the high CO₂ emissions related to the production of ordinary Portland cement (OPC) led to research efforts on the development of eco-efficient alternative binders. Geopolymers constitute promising inorganic binders alternative to OPC which are based on aluminosilicates by-products and alkali activators. The geopolymerization technology of aluminosilicates is a complex chemical process evolving dissolution of raw materials, transportation, orientation and polycondensation of the reaction products. Classical two part geopolymers could become more eco-efficient with a lower CO₂ footprint if sodium silicate usage is avoided. Besides current geopolymeric mixes can suffer from efflorescence originated by the fact that alkaline or soluble silicates that are added during processing cannot be totally consumed during geopolymerisation. Therefore, new and improved geopolymer mixes are needed. One-part geopolymers (sodium silicate free) were first proposed in 2007. However, very few papers were published on these materials. This paper presents experimental results on the durability performance of one-part geopolymers concerning water absorption, penetration of chloride, carbonation resistance and resistance to acid attack. Hydration products results assessed by FTIR spectra are also presented.

Increasing construction and demolition waste (CDW) and the large amount of energy consumption in the building operation process are high-profile issues at present. In the construction industry, recycled aggregated (RA) from CDW can be reutilized in construction, along with green materials, for example, as a road base layer, as aggregate in concrete, etc. Phase change materials (PCM) are often used as building materials due to their good latent heat storage properties. With the use of RA as a matrix to absorb PCM, a thermal performance aggregate can be obtained. This work studied the physical properties of RA from Portugal and combined PCM with RA to prepare a green thermal aggregate through two methodologies using a vacuum and atmospheric pressure. The green aggregate was used in concrete to observe its effect on the compressive strength of concrete. The results showed that the amount of PCM absorbed by the RA mainly depends on the porosity of the matrix material. At the same time, the volume expansion coefficient of PCM was 2.7%, which was not enough to destroy the RA. Ultimately, as the amount of green thermal aggregate increases, the compressive strength of concrete decreases. Green thermal aggregate prepared under vacuum conditions has a greater negative impact on the compressive strength of concrete.

The use of waste as supplementary cementitious materials (SCMs) in concrete is already widespread, with glass waste being an increasingly used option. The utilization of glass waste as a partial substitute for cement in small proportions has shown satisfactory outcomes. Nevertheless, substituting cement in high proportions requires further investigation. Experimental research was carried out on the mechanical and durability properties of concrete with the replacement of cement by glass powder (GP), at a high volume equal to 50%. Binder content (cement plus GP) varied from 300 to 500 kg/m³. The results are promising regarding the use of the high volume of GP in high-performance concretes. The specimens with 500 kg/m³ of binder (50% of which was GP-G250) achieved almost 55 MPa at 28 days. The specimen with the lowest resistance was G150, with 32 MPa. This result may be related to the high pozzolanic activity index of the used GP. The specimens with GP showed satisfactory performance regarding chloride migration, with diffusion coefficients always below those of the reference specimens. The G250 concrete showed a reduction of 58%. Regarding open porosity, concretes with 50% GP had a lower porosity than the reference concretes. The smallest reduction (21%) occurred in the G150 concrete. The reduction in porosity provided by the fineness of the GP may be the main cause of this high performance. Concerning capillary absorption, the GP concretes have a reduction that varies between 47% for G150 and 67% for G250. This fact may be related to the existence of a larger quantity of larger-sized capillary pores in the reference concretes.